Coal gangue (CG) is a residual product from coal mining and washing processes. The reutilization of CG to produce geopolymers is a low-carbon disposal strategy for this material. In this study, the calcined CG (CG_700°C) was used as aluminosilicate precursors, and the effects of alkali activators (i.e., Na₂SiO₃/NaOH, NaOH concentration, and liquid–solid) on the mechanical characteristics and microstructure of CG_700°C-based geopolymers were investigated. The findings indicated that the specimens with a liquid–solid ratio of 0.50 (G_2.0-10-0.50) exhibited a compact microstructure and attained a compressive strength of 24.75 MPa. Moreover, increasing the Na₂SiO₃/NaOH mass ratio has shortened the setting times and facilitated geopolymer gel formation, resulting in a denser microstructure and improved compressive strength. The higher NaOH concentrations of alkali activators facilitated the dissolution of CG_700°C particles, and the geopolymerization process was more dependent on the condensation of SiO₄ and AlO₄ ions, which promoted the formation of geopolymer networks. Conversely, an increase in the liquid–solid ratio from 0.50 to 0.65 had a negative impact on compressive strength enhancement, impeding the polycondensation rate. Examination through scanning electron microscopy and mercury intrusion porosimetry revealed that employing a lower Na₂SiO₃/NaOH mass ratio (G_1.2-10-0.55), smaller NaOH concentrations (G_2.0-8-0.55), and a higher liquid–solid ratio (G_2.0-10-0.65) led to the presence of larger pores, resulting in decreased 28 days compressive strength values (15.87 MPa, 13.25 MPa, and 14.92 MPa, respectively), and a less compact structure. The results suggest that the performance of CG_700°C-based geopolymers is significantly influenced by alkali activators.

Steel–ultra-high-performance concrete (UHPC) composite beams offer numerous advantages, such as structural self-weight reduction, bending stiffness improvement, and tensile cracking limitation in slabs. However, few studies have focused on the shear performance of short stud shear connectors in steel–UHPC composite structures. To this end, push-out tests were carried out to evaluate the effect of slab thickness, stud diameter, and casting method on the failure mode, load–slip relationship, ultimate shear strength, shear stiffness, and ductility. The test results indicate that by increasing the slab thickness from 50 to 75 mm, the stud shear capacity and initial shear stiffness were improved by 11.38% and 23.28%, respectively. The stud shear capacity and initial shear stiffness for specimens with stud diameters of 25 mm were 1.29 and 1.23 times that of their 22-mm-diameter counterparts. In addition, adopting precast UHPC slabs could achieve comparative shear resistance (94.91%) but a better slip capacity (108.94%) than those containing conventional monolithic cast slabs. Based on the experimental results, a finite element (FE) model was established to reflect the plastic behavior of the tests and the damage process in the short stud shear connectors. Based on the validated FE model, a parameter study was then performed to further explore the influence of the stud diameter, stud tensile strength, steel beam tensile strength, monolithic slab concrete strength, precast slab concrete strength, and shear pocket concrete strength on the shear performance of short studs in steel–UHPC composite structures.

By reutilizing industrial byproducts, inorganic cementitious alkali-activated materials (AAMs) contribute to reduced energy consumption and carbon dioxide (CO₂) emissions. In this study, coal gangue (CG) blended with ground granulated blast furnace slag (GGBFS) was used to prepare AAMs. The research focused on analyzing the effects of the GGBFS content and alkali activator (i.e., Na₂O mass ratio and alkali modulus [SiO₂/Na₂O]) on the mechanical properties and microstructures of the AAMs. Through a series of spectroscopic and microscopic tests, the results showed that the GGBFS content had a significant influence on AAM compressive strength and paste fluidity; the optimal replacement of CG by GGBFS was 40–50%, and the optimal Na₂O mass ratio and alkali modulus were 7% and 1.3, respectively. AAMs with a 50% GGBFS content exhibited a compact microstructure with a 28 d compressive strength of 54.59 MPa. Increasing the Na₂O mass ratio from 6% to 8% promoted the hardening process and facilitated the formation of AAM gels; however, a 9% Na₂O mass ratio inhibited the condensation of SiO₄ and AlO₄ ions, which decreased the compressive strength. Increasing the alkali modulus facilitated geopolymerization, which increased the compressive strength. Microscopic analysis showed that pore size and volume increased due to lower Na₂O concentrations or alkali modulus. The results provide an experimental and theoretical basis for the large-scale utilization of AAMs in construction.

The utilization of waste rubber as a viable option for manufacturing building materials holds great significance for the sustainable development of the construction industry. This study explores the addition of two additives, fly ash (FA) and glass fiber (GF), to rubberized mortar in order to improve its performance. The impact of different waste rubber powder (RP) replacement rates and modified additive dosages on the performance of rubberized mortar, including fluidity, mechanical properties, drying shrinkage, impact resistance, and thermal insulation properties, was investigated. Furthermore, the analytic hierarchy process (AHP) was adopted to study the priorities of the rubberized mortar modified by FA and GF. The results indicate that the addition of RP leads to a decrease in mortar fluidity, mechanical properties, and drying shrinkage. However, it can enhance its impact resistance and thermal insulation properties. The additives, FA and GF, have a significant influence on the properties of rubberized mortar. By means of AHP method analysis, this study concludes that the optimal comprehensive properties of FA- and GF-modified rubberized mortar can be achieved by replacing 10% of sand with RP and using 10% FA and 0.4% GF. This study presents a configuration method for modified thermal insulation rubberized mortar, and it may lead to FA and GF being considered potential candidates for developing environmentally friendly building materials.

With rapid urban development, natural aggregate resources have become scarce and a large number of ageing buildings are being demolished, which has resulted in a significant reduction in natural resources and a large increase in construction waste. Therefore, the reuse of solid waste, including waste powder and recycled aggregate, has attracted more and more attention. Additionally, as a prominent way to alleviate the urban heat island effect and manage stormwater runoff, pervious concrete has been widely studied and applied. In this paper, the effects of waste powder (fly ash, volcanic powder and blast furnace slag) and recycled aggregate (recycled concrete aggregate and recycled brick aggregate) on the mechanical properties, water permeability, water filtration and durability of pervious concrete are summarized and introduced, and some prospects are put forward. From the literature review, it can be found that adding the appropriate amount of solid waste or applying proper treatment methods to solid waste will not bring negative effects; rather, it would even improve the performance attributes of pervious concrete. Therefore, the use of solid waste in pervious concrete has great potential for urban construction and environmental protection.