The safety of the use of construction facilities should be a priority in today’s busy world, where it is not difficult to get involved in an accident. Most of them, due to the pace at which we live today, are caused by slips, trips, and falls. This work presents a detailed analysis of the resistance of ceramic floors to these events, taking into account the surface properties and conditions (dry/wet), which, as presented, have a significant impact on the final slip resistance values. This study also investigates the relationship between surface roughness and anti-slip properties. According to the obtained results, it can be concluded that the surface roughness is not the main determinant of slip resistance, and the final value of it is influenced by many components that should be considered together and not be neglected when designing the surface finish. Furthermore, based on experimental measurements, it can be noted that the highest slip resistance in both wet and dry conditions showed the unglazed tiles with lapatto finish and the glazed tiles without any extra finish.

An athlete’s performance depends not only on the shoes they wear but also on the surface used in sports facilities. In addition, it can significantly contribute to reducing injuries, which are easy to get during sports competitions. In the present study, we wanted to investigate whether recycled styrene butadiene rubber (SBR) and ethylene propylene diene monomer (EPDM) could be used in the production of sports surfaces. For this purpose, we designed three different sports surfaces: (1) SBR covered with a thin EPDM spray layer on the top, (2) clean EPDM, and (3) bottom SBR layer with the top layer of EPDM. The test program of these surfaces included in its scope: shock absorption, vertical deformation, tensile strength, abrasion resistance, and slip resistance tests. Our research also involved the influence of the substrate under surface, temperature, and surface conditions. Presented results show that both materials, in the right proportions, can be used in the production of sports surfaces.

This study investigates the effect of accelerated aging on the microstructure and surface properties of synthetic sports surfaces, with the goal of developing a more representative laboratory simulation method. Three common types of polyurethane-based sports surfaces were examined: (1) a dual-layer SBR base with a thin EPDM spray topcoat; (2) a single-layer EPDM surface with a smooth finish; and (3) a dual-layer “sandwich” structure with a rough EPDM upper layer. Samples were tested for slip resistance (PTV), abrasion resistance, and surface morphology using SEM, as well as surface roughness and tensile properties before and after aging. Method combining UV radiation and water spray was introduced and evaluated. Microstructural analysis with roughness measurements revealed surface degradation in all materials, with more extensive damage observed in the UV + spray cycle. Slip resistance results showed reduced performance in dry conditions and improved values in wet conditions post-aging. The single-layer EPDM surface demonstrated the highest initial dry PTV, while the dual-layer with spray had the lowest. After aging, all surfaces exhibited smaller differences between dry and wet performance but no longer met dry condition standards. These results may guide future revisions of performance testing standards and contribute to the development of safer, longer-lasting synthetic sports surfaces.

This research presents a comprehensive evaluation of semi-elastic polyurethane adhesives used for bonding wooden flooring, with a particular focus on both domestic (oak) and exotic hardwood species (teak, iroko, wenge, merbau). Given the increasing interest in sustainable construction practices and the growing use of diverse wood species in flooring systems, this study aimed to assess the mechanical, morphological, and surface properties of adhesive joints under both standard laboratory and thermally aged conditions. Mechanical testing was conducted according to PN-EN ISO 17178 standards and included shear and tensile strength measurements on wood–wood and wood–concrete assemblies. Specimens were evaluated in multiple aging conditions, simulating real-world application environments. Shear strength increased post-aging, with the most notable improvement observed in wenge (21.2%). Tensile strength between wooden lamellas and concrete substrates remained stable or slightly decreased (up to 18.8% in wenge), yet all values stayed above the 1 MPa minimum requirement, confirming structural reliability. Surface properties of the wood species were characterized through contact angle measurements and 3D optical roughness analysis. Teak exhibited the highest contact angle (74.9°) and the greatest surface roughness, contributing to mechanical interlocking despite its low surface energy. Oak and iroko showed high wettability and balanced roughness, supporting strong adhesion. Scanning electron microscopy (SEM) revealed stable adhesive penetration across all species and aging conditions, with no signs of delamination or interfacial failure. The study confirms the suitability of polyurethane adhesives for durable, long-lasting bonding in engineered and solid wood flooring systems, even when using extractive-rich or dimensionally sensitive tropical species. The results emphasize the critical role of surface morphology, wood anatomy, and adhesive compatibility in achieving optimal bond performance. These findings contribute to improved material selection and application strategies in flooring technology. Future research should focus on bio-based adhesive alternatives, chemical surface modification techniques, and in-service performance under cyclic loading and humidity variations to support the development of eco-efficient and resilient flooring systems.