A responsible approach towards sustainable development requires the use of environmentally friendly, low-carbon, and energy-intensive materials. One positive way is to use glass waste as a replacement for fine natural aggregate. For this purpose, the effects of adding glass cullet to the mechanical properties of mortar were carried out. The glass aggregate made from recycled post-consumer waste glass (food, medicine, and cosmetics packaging, including mostly bottles), were used. This experimental work included four different contents of fine glass cullet (5, 10, 15, and 20 wt.% of fine aggregate). The compressive, flexural, and split tensile strengths were evaluated. Moreover, the modulus of elasticity and Poisson coefficient were determined. The addition of glass sand aggregate increases the mechanical properties of mortar. When comparing the strength, the obtained improvement in split tensile strength was the least affected. The obtained effect for the increased analysed properties of the glass sand aggregate content has been rarely reported. Moreover, it was determined that by increasing the recycled glass sand aggregate content, the density of mortar decreased. In addition, the relationships between the properties for mortar containing glass sand aggregate were observed.

High-performance concrete has low tensile strength and brittle failure. In order to improve these properties of unreinforced concrete, the effects of adding recycled polypropylene fibers on the mechanical properties of concrete were investigated. The polypropylene fibers used were made from recycled plastic packaging for environmental reasons (long degradation time). The compressive, flexural and split tensile strengths after 1, 7, 14 and 28 days were tested. Moreover, the initial and final binding times were determined. This experimental work has included three different contents (0.5, 1.0 and 1.5 wt.% of cement) for two types of recycled polypropylene fibers. The addition of fibers improves the properties of concrete. The highest values of mechanical properties were obtained for concrete with 1.0% of polypropylene fibers for each type of fiber. The obtained effect of an increase in mechanical properties with the addition of recycled fibers compared to unreinforced concrete is unexpected and unparalleled for polypropylene fiber-reinforced concrete (69.7% and 39.4% increase in compressive strength for green polypropylene fiber (PPG) and white polypropylene fiber (PPW) respectively, 276.0% and 162.4% increase in flexural strength for PPG and PPW respectively, and 269.4% and 254.2% increase in split tensile strength for PPG and PPW respectively).

The progressive increase in the amount of glass waste produced each year in the world made it necessary to start the search for new recycling methods. This work summarizes the experimental results of the study on mortar samples containing dispersed reinforcement in the form of glass fibers, fully made from melted glass waste (bottles). Mortar mixes were prepared according to a new, laboratory-calculated recipe containing glass fibers, granite as aggregate, polycarboxylate-based deflocculant and Portland cement (52.5 MPa). This experimental work involved three different contents (600, 1200, and 1800 g/m³) of recycled glass fibers. After 28 days, the mechanical properties such as compressive, flexural, and split tensile strength were characterized. Furthermore, the modulus of elasticity and Poisson coefficient were determined. The initial and final setting times, porosity, and pH of the blends were measured. Images of optical microscopy (OM) were taken. The addition of glass fibers improves the properties of mortar. The highest values of mechanical properties were obtained for concrete with the addition of 1800 g/m³ of glass fibers (31.5% increase in compressive strength, 29.9% increase in flexural strength, and 97.6% increase in split tensile strength compared to base sample).

The variety of approaches to tackle climate change reflects the size of this global problem. No technology will act as a panacea to cure the greenhouse gas emissions problem, but new building materials with byproducts or even wastes have the potential to play a major role in reducing the environmental impacts of the building sector. In this study, three potential solutions of concrete with dispersed reinforcement in the form of recycled fibers (polypropylene, glass and steel) were examined. The aim is to present a detailed analysis of the thermal properties of new building materials in an experimental approach. Concrete mixtures were prepared according to a new, laboratory-calculated recipe containing granite aggregate, a polycarboxylate-based deflocculant, Portland cement (52.5 MPa) and fibers. This experimental work involved three different contents of each fiber (0.5%, 0.75% and 1.0 wt.%), and all tests were carried after the complete curing cycle of concrete (28 days).

The safety of the use of construction facilities should be a priority in today’s busy world, where it is not difficult to get involved in an accident. Most of them, due to the pace at which we live today, are caused by slips, trips, and falls. This work presents a detailed analysis of the resistance of ceramic floors to these events, taking into account the surface properties and conditions (dry/wet), which, as presented, have a significant impact on the final slip resistance values. This study also investigates the relationship between surface roughness and anti-slip properties. According to the obtained results, it can be concluded that the surface roughness is not the main determinant of slip resistance, and the final value of it is influenced by many components that should be considered together and not be neglected when designing the surface finish. Furthermore, based on experimental measurements, it can be noted that the highest slip resistance in both wet and dry conditions showed the unglazed tiles with lapatto finish and the glazed tiles without any extra finish.