Zinc and zinc alloys have been studied due to their corrosion properties as potentially biodegradable materials. In this study, a zinc/hydroxyapatite composite (Zn/HA) containing 16 wt % HA was prepared by spark plasma sintering and characterized in detail. The microstructure, mechanical and corrosion properties were studied and the mutual relations between properties and microstructure were found. The porosity was evaluated to be approximately 18%. The mechanical properties (ultimate compression strength = 65 MPa and ultimate flexural strength = 120 MPa) are sufficient for the potential scaffolding and augmentation of cancellous bone. The flexural properties of these materials were measured for the first time. Immersion tests and subsequent analyses confirmed no direct participation of hydroxyapatite in the corrosion process and an ideal corrosion rate of approximately 0.4 mm/year. The amount of released zinc was between 4–6 mg/day corresponding with the maximal usable surface area of 25 cm². All the results suggest that the Zn/HA composite is suitable as a potential biodegradable material (from the point of view of mechanical and corrosion properties) for the replacement of cancellous bones.

Electrochemical treatment by means of direct current (DC) is usually used as a measure for steel rebar corrosion protection, e.g., cathodic protection (CP), electrochemical chloride extraction (ECE), and re-alkalization (RA). However, the passage of an electrical charge through the pore system of concrete or mortar, coupled with the migration of ions, concentration changes, and resulting phase changes, may alter its chloride penetration resistance and, subsequently, the time until rebar corrosion activation. Porosity changes in hardened Portland cement mortar were studied by means of mercury intrusion porosimetry (MIP) and electrochemical impedance spectroscopy (EIS), and alterations in the mortar surface phase composition were observed by means of X-ray diffraction (XRD). In order to innovatively investigate the impact of DC treatment on the properties of the mortar–electrolyte interface, the cathode-facing mortar surface and the anode-facing mortar surface were analyzed separately. The corrosion of steel coupons embedded in DC-treated hardened mortar was monitored by means of the free corrosion potential (E_oc) and polarization resistance (R_p). The results showed that the DC treatment affected the surface porosity of the hardened Portland cement mortar at the nanoscale. Up to two-thirds of the small pores (0.001–0.01 µm) were replaced by medium-sized pores (0.01–0.06 µm), which may be significant for chloride ingress. Although the porosity and phase composition alterations were confirmed using other techniques (EIS and XRD), corrosion tests revealed that they did not significantly affect the time until the corrosion activation of the steel coupons in the mortar.

The technology of molten salt oxidation (MSO) is a thermal treatment process mainly used for reprocessing of hazardous organic waste. This technology is considered as an alternative to the conventional incineration processes. The principle of the whole technology is based on flameless oxidation of materials in the molten salt with the consequent capture of gaseous products in molten alkaline salts. The melts with low melting point and high viscosity, such as a ternary mixture of carbonates Na2CO3, K2CO3, and Li2CO3, are the most used in this technology. However, the molten salts create a very corrosive environment for metal and ceramic materials, so the main aim of this experimental work was to determine the resistance of corundum samples, which were prepared by plasma spraying, and to find out its potential use as the protection of the reactor metal surface.