TiO2 is a common inorganic filter used in sunscreens due to its photoprotective effect on the skin against UV radiation. However, the use of this kind of material in cosmetics is limited by its inherent photocatalytic activity. It is known that coating on TiO2 surface can improve some features. Although, many of the methodologies used for this purpose are still laborious and time-consuming. Thus, this work reports a novel, easy, cheap and fast strategy to coat TiO2 particles by using a sonochemistry approach, aiming to decrease photocatalytic activity and to enhance colloidal stability. For this proposal, SiO2, Al2O3, ZrO2 and sodium polyacrylate (PAANa) were used to tune the surface of commercial TiO2 particles and they were applied in a sunscreen formulation. The samples were characterized by XRPD, FT-IR, DLS, EDS, SEM and TEM. The photocatalytic activity and UV-shielding ability were also evaluated. The sunscreen formulations were prepared and characterized by zeta potential, DLS, and Sun Protection Factor (SPF). FT-IR, EDS, and charge surface of the particles confirmed the success of the sonochemistry coating. Additionally, TiO2@Al2O3, TiO2@SiO2 and TiO2@PAANa show a lower photocatalytic activity than original TiO2 with similar UV-shielding ability. The sunscreens produced with the coated TiO2 have similar SPF to the one with commercial TiO2. Specifically, the sunscreen with TiO2@PAANa shows an increase in colloidal stability. Herein, the incorporation of the sonochemical-coated TiO2 particles in sunscreen formulations may produce sunscreens with better aesthetic appearance and a greater health security due to its lower free radicals production.

In this study, flotation tests were conducted on a laboratory scale using a sample of microcrystalline graphite ore from the Canindé region, Ceará, Brazil. The objective was to investigate the grinding time, reagent dosage, and purification process for obtaining graphene-based nanomaterials. Natural graphite has a stacked planar structure and exhibits polymorphism with rhombohedral, hexagonal, and turbostratic geometries, characteristics that directly influence its properties and technological applications. The results demonstrated that it was possible to obtain rougher concentrate with a graphite carbon content of 23.4% and a recovery of 86.4%, using a grinding time of 7.5 min and reagent dosages of 150 g/t of kerosene and 100 g/t of Flotanol D-25. This flotation process resulted in a graphite concentrate with 76.6% graphite carbon content. To increase the purity of the concentrate and expand its industrial applications, the graphite was purified in an alkaline autoclave using the hydrothermal method. In the next stage, acid leaching was performed, and this chemical treatment destabilized the regular stacking of the graphite layers, promoting the formation of graphene-like nanoplates, including monolayer graphene. Thus, the nanomaterials obtained through the process developed in this study have potential for various innovative applications, such as lithium-ion batteries, electric vehicles, and two-dimensional graphene-based materials.

In this study, flotation tests were conducted on a laboratory scale using sample of microcrystalline graphite ore from the Canindé region, Ceará, Brazil. The objective was to investigate the grinding time, reagent dosage, and purification process for obtaining graphene-based nanomaterials. Natural graphite has stacked planar structure and exhibits polymorphism with rhombohedral, hexagonal, and turbostratic geometries, characteristics that directly influence its properties and technological applications. The results demonstrated that it was possible to obtain rougher concentrate with a graphite carbon content of 23.4% and a recovery of 86.4%, using grinding time of 7.5 minutes and reagent dosages of 150 g/t of kerosene and 100 g/t of Flotanol D-25. This flotation process resulted in a graphite concentrate with 76.6% graphite carbon content. To increase the purity of the concentrate and expand its industrial applications, the graphite was purified in an alkaline autoclave using the hydrothermal method. In the next stage, acid leaching was performed, and this chemical treatment destabilized the regular stacking of the graphite layers, promoting the formation of graphene-like nanoplates, including monolayer graphene. Thus, the nanomaterials obtained through the process developed in this study have potential for various innovative applications, such as lithium-ion batteries, electric vehicles, and two-dimensional graphene-based materials.

The objective of this work was to produce, characterize and evaluate antifungal activity of agarose nanostructured films with silver nanoparticles using glucose...