In this communication, it was evaluated the production of fatty acid ethyl ester (FAAE) from the free fatty acids of babassu oil catalyzed by lipase from Rhizomucor miehei (RML) immobilized on magnetic nanoparticles (MNP) coated with 3-aminopropyltriethoxysilane (APTES), Fe₃O₄@APTES-RML or RML-MNP for short. MNPs were prepared by co-precipitation coated with 3-aminopropyltriethoxysilane and used as a support to immobilize RML (immobilization yield: 94.7 ± 1.0%; biocatalyst activity: 341.3 ± 1.2 U_p–NPB/g), which were also activated with glutaraldehyde and then used to immobilize RML (immobilization yield: 91.9 ± 0.2%; biocatalyst activity: 199.6 ± 3.5 U_p–NPB/g). RML-MNP was characterized by X-Ray Powder Diffraction (XRPD), Fourier Transform-Infrared (FTIR) spectroscopy and Scanning Electron Microscope (SEM), proving the incorporation and immobilization of RML on the APTES matrix. In addition, the immobilized biocatalyst presented at 60°C a half-life 16–19 times greater than that of the soluble lipase in the pH range 5–10. RML and RML-MNP showed higher activity at pH 7; the immobilized enzyme was more active than the free enzyme in the pH range (5–10) analyzed. For the production of fatty acid ethyl ester, under optimal conditions [40°C, 6 h, 1:1 (FFAs/alcohol)] determined by the Taguchi method, it was possible to obtain conversion of 81.7 ± 0.7% using 5% of RML-MNP.

Magneto-dielectric composites are interesting advanced materials principally due to their potential applications in electronic fields, such as in microstrip antennas substrates. In this work, we developed superparamagnetic polymer-based films using the biopolymeric matrices chitosan (Ch), cellulose (BC) and collagen (Col). For this proposal, we synthesized superparamagnetic iron oxide nanoparticles (SPIONs) functionalized with polyethyleneimine with a cheap method using sonochemistry. Further, the SPIONs were dispersed into polymer matrices and the composites were evaluated regarding morphology, thermal, dielectric and magnetic properties and their application as microstrip antennas substrates. Microscopically, all tested films presented a uniform dispersion profile, principally due to polyethyleneimine coating. Under an operating frequency (f_o) of 4.45 GHz, Ch, BC and Col-based SPION substrates showed moderate dielectric constant (ε′) values in the range of 5.2–8.3, 6.7–8.4 and 5.9–9.1, respectively. Furthermore, the prepared films showed no hysteresis loop, thereby providing evidence of superparamagnetism. The microstrip antennas showed considerable bandwidths (3.37–6.34%) and a return loss lower than −10 dB. Besides, the f_o were modulated according to the addition of SPIONs, varying in the range of 4.69–5.55, 4.63–5.18 and 4.93–5.44 GHz, for Ch, BC and Col-based substrates, respectively. Moreover, considering best modulation of ε′ and f_o, the Ch-based SPION film showed the most suitable profile as a microstrip antenna substrate.

O Ensino de Geometria Molecular com Materiais de Baixo Custo