Polyamides (PAs) are widely used as barrier materials in offshore oil and gas (O&G) equipment due to their mechanical strength and chemical resistance. However, long-term exposure to hydrogen sulfide scavengers (H₂S-SCVs) may significantly affect their physicochemical properties. Previous studies using thermal analysis and ¹H time-domain NMR (¹H TD-NMR) suggest that ethoxylated H₂S-SCVs impose molecular constraints, increasing the glass transition temperature (T_g) and reducing chain mobility above T_g. The present study builds upon these findings using a multi-technique analytical approach, including FTIR, Raman, ¹H DQ-TD-NMR, and ¹³C solid-state NMR (ssNMR), to provide a more comprehensive understanding of the molecular alterations in PA materials. The results clearly demonstrate that H₂S-SCV exposure leads to the progressive exudation of plasticizers from the PA matrix. This plasticizer loss is a key factor contributing to the observed shift in Tg and the reduction in molecular mobility. ¹H DQ-TD-NMR data confirmed an increase in the density of dynamically constrained chains over time and allowed for the characterization of heterogeneity in these constraints throughout the PA matrix. Moreover, ¹³C ssNMR spectra revealed the presence of immobilized H₂S-SCV chemical groups within the polymer matrix, strongly supporting the early statement that the mobility constraints observed in ¹H DQ-TD-NMR are associated with the formation of crosslinks induced by the H₂S-SCV: H₂S-SCV acts as a crosslinking agent. Taken together, our findings indicate that both plasticizer loss and H₂S-SCV-induced crosslinking contribute significantly to the microstructural evolution of PAs when exposed to ethoxylated H₂S-SCVs, offering important insights into their degradation mechanisms and long-term behavior in aggressive operational environments.