High-entropy alloy (HEA) coatings of CoCrFeNiTiAl_x (x = 0, 0.5, 1, 1.5, 2) were prepared on the surface of AISI1045 steel by laser cladding. The effects of the Al content on the microstructure, composition, phase constitution, and wear and corrosion resistance of the coatings were investigated. The results showed that when increasing the Al element content from 0 to 0.5, the phase constitution of the CoCrFeNiTiAl_x coating changed from a single Face-centered cubic (FCC) phase to Body-centered cubic 1 (BCC1) and Body-centered cubic 2 (BCC2) phases, with a small amount of Laves phase, which obviously improved the friction and corrosion resistance of the coating. With further enhancing of the Al content, the amount of BCC1 phase increased, while the BCC2 phase and the Laves phase decreased. The CoCrFeNiTiAl₂ HEA coating transformed into a single BCC1 phase, with retrogressive wear and corrosion resistance. It was found that the Al_0.5 alloy coating exhibits excellent wear resistance, high hardness, and corrosion resistance in a 3.5 wt.% NaCl solution. Furthermore, the effect of the Al content on the microstructure, phase, and the relating properties of the CoCrFeNiTiAl_x HEA coatings is also discussed.

Titanium alloys are widely used in aerospace, chemical, biomedical and other important fields due to outstanding properties. The mechanical behavior of Ti alloys depends on microstructural characteristics and type of alloying elements. The purpose of this study was to investigate the effects of different Cu contents (2.5 wt.%, 7 wt.% and 14 wt.%) on mechanical and frictional properties of titanium alloys. The properties of titanium alloy were characterized by tensile test, electron microscope, X-ray diffraction, differential scanning calorimetry, reciprocating friction and wear test. The results show that the intermediate phase that forms the eutectoid structure with α-Ti was identified as FCC Ti₂Cu, and no primary β phase was formed. With the increase of Cu content, the Ti₂Cu phase precipitation in the alloy increases. Ti₂Cu particles with needle structure increase the dislocation pinning effect on grain boundary and improve the strength and hardness of titanium alloy. Thus, Ti-14Cu shows the lowest elongation, the best friction and wear resistance, which is caused by the existence of Ti₂Cu phases. It has been proved that the mechanical and frictional properties of Ti-Cu alloys can be adjusted by changing the Cu content, so as to better meet its application in the medical field.

A CoCrCuFeNiTi_0.8 high-entropy alloy was prepared using directional solidification techniques at different withdrawal rates (50 μm/s, 100 μm/s, 500 μm/s). The results showed that the microstructure was dendritic at all withdrawal rates. As the withdrawal rate increased, the dendrite orientation become uniform. Additionally, the accumulation of Cr and Ti elements at the solid/liquid interface caused the formation of dendrites. Through the measurement of the primary dendrite spacing (λ₁) and the secondary dendrite spacing (λ₂), it was concluded that the dendrite structure was obviously refined with the increase in the withdrawal rate to 500 μm/s. The maximum compressive strength reached 1449.8 MPa, and the maximum hardness was 520 HV. Moreover, the plastic strain of the alloy without directional solidification was 2.11%, while the plastic strain of directional solidification was 12.57% at 500 μm/s. It has been proved that directional solidification technology can effectively improve the mechanical properties of the CoCrCuFeNiTi_0.8 high-entropy alloy.