Stainless steel grade 430 is a type of soft magnetic electromagnetic material with rapid magnetization and demagnetization properties. Considering the delay phenomenon during operation, this study selected 430 stainless steel as the material and explored various metallurgical methods such as magnetic annealing and the addition of Mo as well as increasing the Si content to investigate the microstructure, mechanical behavior, and magnetic properties of each material, aiming to improve the magnetic properties of 430 stainless steel. Experimental results showed that the four electromagnetic steel materials (430F, 430F-MA, 434, and KM31) had equiaxed grain matrix structures, and excellent tensile and elongation properties were observed for each specimen. Additionally, the magnetic properties of the 430F specimen were similar under the DC and AC-10 Hz conditions. According to the hysteresis curves under different AC frequencies (10, 100, 1000 Hz), both magnetic annealing and the addition of Mo could reduce the Bm, Br, and Hc values of the raw 430F material. Increasing the Si content resulted in a decrease in Hc values and an increase in Bm and Br values.

430 stainless steel exhibits soft magnetic properties, excellent formability, and corrosion resistance, making it widely used in industrial applications. This study investigates the effects of different cold working rates on the properties of 430 stainless steel subjected to various magnetic annealing atmospheres (F-1.5Si, F-1.5Si-10%, F-1.5Si-40%, F-1.5Si-10% (MA), F-1.5Si-40% (MA), F-1.5Si-10% (H₂), and F-1.5Si-40% (H₂)). The results indicate that increasing the cold working rate improves the material’s mechanical properties; however, it negatively impacts its magnetic and corrosion resistance properties. Additionally, the magnetic annealing process improves the mechanical properties, while atmospheric magnetic annealing optimizes the overall magnetic performance. In contrast, magnetic annealing in a hydrogen atmosphere does not enhance the magnetic properties as effectively as atmospheric magnetic annealing. Still, it promotes the formation of a protective layer, preserving the mechanical properties and providing better corrosion resistance. Furthermore, regardless of whether magnetic annealing is conducted in an atmospheric or hydrogen environment, materials with 10% cold work rate (F-1.5Si-10% (MA) and F-1.5Si-10% (H₂)) exhibit the lowest coercive force (286 and 293 A/m in the 10 Hz test condition), making them ideal for electromagnetic applications.