Nickel oxide (NiO) is one of the most popular hydrogenation catalysts. In heterogeneous catalysis, nickel oxide is used, for example, as a suitable methanation catalyst in the Fischer–Tropsch reaction not only for CO hydrogenation but also in the modified Fischer–Tropsch reaction with CO₂. However, CH₄ selectivity and CO₂ conversion strongly depend on NiO micro- (MPs) and nanoparticles’ (NPs) shape, size, and surface area. In this study, the synthesis of NiO micro- and nanoparticles was conducted using the simple solvothermal method. Different morphologies (microspheres, sheet clusters, hexagonal microparticles, and nanodiscs) were prepared using this method with different solvents and stabilizers. The prepared catalysts were tested in the hydrogenation of CO₂ in a gas phase with excellent conversion values and high selectivity to produce CH₄. The best results were obtained with the NiO with disc or sphere morphology, which produced methane with selectivity at a level near 100% and conversion close to 90%.

Nickel and nickel oxide are widely used as heterogeneous catalysts in various processes involving the hydrogenation or reduction of organic compounds, and also as excellent methanation catalysts in the hydrogenation of CO₂. As heterogeneous catalysis is a surface-dependent process, nickel compounds in the form of microparticles (MPs), and particularly nanoparticles (NPs), improve the catalytic activity of Ni-based catalysts due to their high specific surface area. Solvothermal synthesis, which has so far been neglected for the synthesis of Ni-based methanation catalysts, was used in this study to synthesize nickel and nickel oxide MPs and NPs with a narrow size distribution. Solvothermal synthesis allows for the control of both the chemical composition of the resulting Ni catalysts and their physical structure by simply changing the reaction conditions (solvent, temperature, or concentration of reactants). Only non-toxic substances were used for synthesis in this study, meaning that the whole synthesis process can be described as environmentally friendly. Solvothermally prepared Ni compounds were subsequently transformed into nickel oxide by means of high-temperature decomposition, and all of the prepared Ni-based compounds were tested as catalysts for CO₂ methanation. The best catalysts prepared in this study exhibited a CO₂ conversion rate of nearly 95% and a selectivity for methane close to 100%, which represent thermodynamic limits for this reaction at the used temperature. These results are commonly achieved with much more complex catalytic composites containing precious metals, while here we worked with pure nickel and its oxides, in the form of micro- or nanoparticles, only.

The growing concentration of CO₂ in the atmosphere is a serious problem, and efforts to counter this issue are thus highly important. One of the possible approaches to solving this problem is the conversion of waste CO₂ into products with added economic value. Methanol is one of these products with vast potential usage. In this study, indium oxide prepared by a simple precipitation method and modified by nanoparticles of metals from the iron triad were tested as possible catalysts to produce methanol by the method of CO₂ hydrogenation. The prepared catalysts demonstrated a strong dependence of their catalytic activity on used metal. The best selectivity for the production of CH₃OH was observed for the Fe/In₂O₃ catalyst at the value of 54.7% at 300 °C. However, due to the higher value of CO₂ conversion, the highest CH₃OH formation rate was observed at a value of 11.3 mmol/(h*g) at 300 °C for a composite of Ni/In₂O₃.