In this study, ternary NiFeP coatings were fabricated on a copper substrate using a simple, fast, and cost-effective electroless deposition method. The coatings were named Ni₈₅Fe₄P₁₂, Ni₈₀Fe₈P₁₂, and Ni₇₅Fe₁₂P₁₂, indicating 4, 8, and 12 at % of Fe, respectively. The surface morphology and composition of the coatings were characterized using scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX). The activity of the prepared coatings was evaluated using the water-splitting reaction to determine the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) in a 1 M KOH electrolyte solution. Electrochemical measurements were carried out in a temperature range from 25 °C to 55 °C. The HER and OER current density values increased by up to 2.58 and 2.13 times, respectively, with temperature increase compared to the result at 25 °C. All three coatings demonstrated activity in both reactions. Ni₈₅Fe₄P₁₂ exhibited the highest catalytic efficiency in the HER, with the overpotential of 340 mV at 10 mAcm⁻² and a Tafel slope of 61 mVdec⁻¹. In the OER, the efficiency of the NiFeP catalysts correlated with their Fe content. The overpotential was 412 mV for Ni₈₀Fe₈P₁₂ and 432 mV for Ni₇₅Fe₁₂P₁₂ at 10 mAcm⁻² with Tafel slopes of 96 and 91 mVdec⁻¹, respectively. This study underscores the critical influence of Fe content on the catalytic efficiency of NiFeP coatings, with reduced Fe content enhancing HER and increased Fe content benefits OER.

The generation of high-purity hydrogen via chemical reaction from hydrogen-rich materials is one of the ways in the alternative energy industry. In this approach, the utilization of catalytic materials that possess the capacity to initiate the decomposition of the starting material and the subsequent release of hydrogen is of paramount importance. In this study, nickel/cobalt-plated copper catalysts (NiCo/Cu) are presented, comprising from 4 to 90 wt.% of cobalt as catalytic materials for hydrogen generation via sodium borohydride (NaBH₄) hydrolysis reaction. The NiCo/Cu catalysts were synthesized via electroless deposition from glycine-based baths, utilizing Ni²⁺ and Co²⁺ ions as metal sources and morpholine borane (MB) as the reducing compound. The catalytic performance in alkaline NaBH₄ hydrolysis was found to correlate with the cobalt loading in the coating. The maximum rate of hydrogen production, which was determined to be 14.22 L min⁻¹ gcat⁻¹, was achieved at 343 K for a catalyst composed of 90 wt.% Co. The reaction proceeded with the activation energy of 52.5 kJ mol⁻¹, while the catalyst exhibited high durability, preserving nearly 88% of its initial activity after five successive reaction cycles. The combination of nickel and cobalt, along with their synergistic effect and high efficiency in the borohydride hydrolysis reaction, makes them promising catalysts.