The adsorption of gold on activated carbon in ammoniacal thiosulfate solution was studied. The variables affecting the adsorption of gold on the carbon included, among others, temperature, concentrations of ammonium hydroxide and thiosulfate, and those of accompanying cations and anions. The apparent activation energy for the adsorption process was estimated to be 19.4 kJ/mol, and this value indicates that the gold adsorption is film diffusion-controlled. It was also found that the rate of initial adsorption rate was fast, when compared to that of the overall adsorption process.

The leaching of copper ores produces a rich solution with metal interferences. In this context, Fe(III), Zn(II), and Mn(II) are three metals contained in industrial copper-rich solutions in high quantities and eventually can be co-extracted with the copper. The purpose of the current study was to determine the feasibly of solvent extraction with the use of ionic liquid methyltrioctyl/decylammonium bis (2,4,4-trimethylpentyl)phosphinate (R₄NCy) as an extractant of Cu(II) in the presence of Fe(III), Zn(II), and Mn(II). In general terms, the results showed a high single extraction efficiency of all the metals under study. In the case of Fe(III) and Zn(II), the extraction was close to 100%. On the contrary, the stripping efficiency was poor to Fe(III) and discrete to Zn(II), but very high to Cu(II) and Mn(II). Finally, the findings of this study suggest that the ionic liquid R₄NCy is feasible for the pre-treatment of the copper solvent extraction process to remove metal impurities such as Fe(III) and Zn(II).

Recent works suggest that the use of ionic liquids in the copper solvent extraction industry is feasible. However, the reports did not use real solutions (or synthetic solutions with various elements). This fact remains poorly established, and the interaction efficiencies are still under study. The objective of this research is to explore the extraction and stripping of the four major elements present in a copper industrial pregnant leach solution (Cu(II), Fe(III), Mn(II), and Zn(II)) using the methyltrioctyl/decylammonium bis(2,4,4-trimethylpentyl)phosphinate (R₄NCy) ionic liquid as an extractant. The work conditions studied in extraction were ionic liquid concentration, initial pH, and O/A ratio, and in stripping were H₂SO₄ concentration and O/A ratio. The test was carried out at room temperature and ambient pressure. High efficiency and selectivity (99.82% and 113,755 over Cu(II), respectively) were observed for Fe(III) extraction over the other elements. Moreover, after the extraction test, significant difficulty in stripping Fe(III) loaded in the ionic liquid was observed (28.7% at 0.5 M of H₂SO₄). Finally, the present study demonstrates that the R₄NCy ionic liquid is not suitable for copper extraction because it has a higher selectivity for Fe(III) and Zn(II).

Se estudió el efecto de las propiedades físicas de un carbón activado, tales como distribución de tamaño de poros, superficie específica, diámetro promedio de poros, en la adsorción de oro desde disoluciones cianuradas, con el oro disuelto a la forma de Au (CN)–2. Para cumplir con los objetivos planteados se trabajó con dos carbones activados: el carbón A, con superficie específica de 985 m2/g, 57 % de microporos y 3,8 nm como diámetro promedio de poros, y el carbón B, con superficie específica de 786 m2/g, 27 % de microporos y 11,6 nm como diámetro promedio de poros; ambos carbones, de forma granular, han sido fabricados a partir de cáscara de coco. Se realizaron ensayos de adsorción batch en un reactor de 500 ml de capacidad, con agitación mecánica a temperatura constante. Se estudiaron los efectos de cationes presentes, tales como Ca2+, Na+, K+ y Li+, de la distribución de tamaño de poros, del diámetro promedio de poros y del área superficial, en la velocidad y cantidad de oro adsorbido en los carbones activados denominados como A y B. Se encontró que las propiedades físicas de un carbón activado constituyen un factor relevante en el proceso de adsorción de oro, en términos de velocidad y cantidad de oro adsorbido. El carbón B, con 786 m2/g de superficie específica, alcanzó una mayor carga por unidad de superficie (0,02 mg Au/m2) en relación al carbón A, de 985 m2/g, el cual alcanzó una carga de 0,01 mg Au/m2, después de 6 h de contacto carbón-disolución. La velocidad de adsorción de oro en ambos carbones fue controlada por transferencia de masa en la película líquida que rodea a las partículas de carbón, a tiempos cortos o cargas pequeñas de oro en las partículas, lejos del equilibrio. Al aplicar un modelo cinético de primer orden, se obtuvo que la razón de las constantes cinéticas para los carbones A y B, es decir, (kB/kA), fluctúa en un valor de 3 para los distintos cationes en estudio. En general, es posible afirmar que la velocidad de adsorción y la cantidad de oro adsorbido aumentan con el aumento de macroporos y con el aumento del diámetro promedio de poros. La presencia de cationes favorece el proceso de adsorción de oro en medio cianuro, especialmente los de mayor valencia.