Despite extensive research on the effect of nitrogen flow rate on titanium nitride (TiN) coating properties, its influence on esthetic and engineering performance through microstructure control remains insufficiently explored. To simultaneously meet the requirements for surface strengthening and decorative esthetics in high-end stainless-steel crafts, TiN coatings were deposited on 304L stainless-steel substrates using multi-arc ion plating. The regulatory mechanisms and synergistic evolution laws of nitrogen flow rates (100, 200, and 300 sccm) on the microstructure, decorative properties (color and gloss), and engineering performance (adhesion strength, hardness, wear resistance, and corrosion resistance) of the coatings were investigated. At a nitrogen flow rate of 200 sccm, the coating exhibited a uniform and dense columnar crystal structure, as well as a saturated golden hue with high surface gloss. Additionally, the film–substrate adhesion, microhardness, tribological properties, and corrosion resistance reached optimal levels. In contrast, excessively low (100 sccm) or high (300 sccm) nitrogen flow rates resulted in coarse particles and blurred grain boundaries owing to uncontrolled droplet ejection or target poisoning, respectively, thereby deteriorating both appearance and engineering performance. These findings can inform the optimization of TiN coatings, enabling the design of surfaces that simultaneously meet esthetic and high-performance engineering requirements.

In our investigation of the influence rules and mechanisms of the building orientation on the surface properties of 316L stainless steel created via selective laser melting, we used X-ray diffractometry, scanning electron microscopy, and electron backscatter diffraction to investigate the phases, microstructures, and textures of specimens. In addition, we employed a digital microhardness tester, friction, and wear-testing apparatus, along with an electrochemical workstation, to examine variations in the surface properties. The results indicated that the surface phase compositions of the specimens with different building orientations were similar; however, they displayed anisotropic behavior in grain size, orientation, and texture. Notably, the surface densification of the specimens at 0°, 30°, 45°, and 60° initially decreased before subsequently increasing. In contrast, the surface roughness showed a pattern of first increasing and then declining. Moreover, the microhardness, wear resistance, and corrosion resistance decreased with an increasing inclination angle.

To improve the surface properties of 40Cr steel, Ni45/Y₂O₃ laser-cladded coatings (L-CCs) were fabricated on the surface of 40Cr steel. The effects of Y₂O₃ addition (0.5%, 1.0%, and 1.5%) on the microstructure, microhardness, residual stress, wear resistance, and corrosion resistance of the L-CCs were systematically investigated. The results indicate that Y₂O₃ has a significant effect on enhancing the corrosion resistance and suppressing the residual stress of the L-CCs, whereas its contribution to the improvement of microhardness and wear resistance is relatively limited. Compared with the single Ni45 L-CC, the L-CC containing 1.0% Y₂O₃ exhibited a 45.9% reduction in corrosion current density and a 79.3% reduction in residual stress. At a Y₂O₃ addition of 0.5%, the microhardness increased by 4.0%, while the average friction coefficient and wear mass loss decreased by 4.8% and 2.6%, respectively, relative to the single Ni45 L-CC. Excessive Y₂O₃ addition reduces the fluidity of materials in the molten pool and deteriorates the microstructural uniformity, thereby weakening or even impairing the surface properties of the L-CCs.

Aluminum alloy 6061 is widely used in the industrial field, but its poor corrosion resistance has a significant impact on the reliability of equipment components. To address the corrosion resistance issue of 6061 aluminum alloy, a novel Ti-Zr-V conversion coating was prepared on its surface in this study, and the conversion parameters were optimized. The morphology, element distribution and content, composition of compounds, and corrosion resistance of the prepared Ti-Zr-V conversion coating were comprehensively analyzed and evaluated using scanning electron microscopy, energy dispersive spectroscopy, X-ray photoelectron spectroscopy, copper sulfate spot test, and electrochemical experiments. The research results showed that the conversion parameters had a significant impact on the corrosion resistance of the conversion coating. The optimal conversion parameters were a pH value of 4.5 and a conversion time of 5 min, with the optimal addition amount of the auxiliary film former NaVO₃ being 0.6 g/L. Under these conditions, the Ti-Zr-V conversion coating prepared was relatively dense, with fewer grooves, the longest spot resistance time, and the best corrosion resistance. Its surface mainly consisted of titanium dioxide, zirconium dioxide, vanadium pentoxide, V₂O₃, aluminum oxide, and a small amount of fluoride compounds. Electrochemical analysis also demonstrated that the corrosion rate of TiZrVCC decreased by approximately 87.12% compared to the aluminum alloy 6061 substrate, providing a theoretical basis and technical support for the further promotion and use of aluminum alloy.