Recently, more sustainable and biodegradable packaging materials have begun to attract attention in food packaging due to major, rising concerns related to plastic usage. This study aims to develop and characterize biodegradable food packaging materials, namely poly(lactic acid) (PLA) and poly(ε-caprolactone) (PCL) enriched with pomegranate peel extract (PoPE). Firstly, the optimal extract selected was a 24 h maceration of PoPE with 60% ethanol, after production with different solvents and methods. PLA- and PCL-based films were produced via melt compounding with the addition of PoPE at different concentrations (1, 3, 5 and 10%, w/w). FTIR confirmed that the PoPE did not modify the chemical backbones of PLA or PCL, with only a more pronounced O–H band in PCL, suggesting mainly non-covalent/physical interactions. UV–Vis spectroscopy showed tunable warm coloration and strong UV shielding with reduced transparency; for PLA ~3–5 wt.%, PoPE enabled near-complete UV blocking, while PCL achieved very high UV protection even at low loadings. PoPE improved toughness in PLA (3–5 wt.%) and maintained ductility in PCL (1–10 wt.%). PoPE-added PLA and PCL films maintained thermal stability up to 10 wt.% according to TGA results. DSC/XRD indicated a matrix-dependent crystallization response. PLA remained largely amorphous, whereas PoPE promoted PCL crystallinity without changing polymer crystal polymorphs. SEM images revealed homogenous dispersion of PoPE in the films.

The present study analyses the changes in antioxidative behavior of biodegradable Poly(lactic acid) (PLA)-based composite films with bioactive additives derived from pomegranate peel, an abundant agricultural by-product rich in antioxidants and antimicrobials. PLA-based composites were prepared by incorporating industrial-grade pomegranate peel powder (PoP) via melt extrusion at concentrations of 1–5 percent by weight (wt.%). For mechanical characterization, the resulting films were subjected to tensile testing. Their thermal properties were further characterized using thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), dynamic oxidation induction temperature measurements (OIT), complemented by Fourier-transform infrared spectroscopy (FT-IR), color analysis, rheology, scanning electron microscopy (SEM), and UV-Vis spectroscopy. Results show that the incorporation of PoP had no significant impact on the characteristic transition temperatures (Tg, Tm, and Tc) of PLA, indicating that the thermal behavior of the polymer matrix was largely preserved. However, while the thermo-oxidative stability of PLA was improved in the presence of PoP, with a maximum at 3 wt.% of PoP, increasing the OIT by 30 °C, the mechanical performance of the composite films was adversely affected, as evidenced by decreased tensile strength and elongation at break indication embrittlement, especially for ≥3 wt.% of PoP. Significant changes were observed in the films’ surface properties, as well as in their color parameters and UV transmittance values. Consequently, while PoP offers potential bioactive functionality for use as a sustainable additive, its content must be carefully optimized to maintain an acceptable balance between functionality and mechanical integrity.