This paper presents sustainable technology for environmentally friendly composite production. Biobased unsaturated polyester resin (b-UPR), synthesized from waste polyethylene terephthalate (PET) glycosylate and renewable origin maleic anhydride (MAnh) and propylene glycol (PG), was reinforced with unmodified and vinyl-modified biosilica nanoparticles obtained from rice husk. The structural and morphological properties of the obtained particles, b-UPR, as well as composites, were characterized by Fourier-transform infrared spectroscopy (FTIR), nuclear magnetic resonance spectroscopy (NMR), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) techniques. The study of the influence of biosilica modification on the mechanical properties of composites was supported by hardness modeling. Improvement of the tensile strength of the b-UPR-based composite at 2.5 wt.% addition of biosilica modified with vinyl silane, named “b-UPR/SiO₂-V” composite, has been achieved with 88% increase. The thermal aging process applied to the b-UPR/SiO₂-V composite, which simulates use over the product’s lifetime, leads to the deterioration of composites that were used as fillers in commercial unsaturated polyester resin (c-UPR). The grinded artificially aged b-UPR composites were used as filler in c-UPR for the production of a table top layer with outstanding mechanical properties, i.e., impact resistance and microhardness, as well as fire resistance rated in the V-0 category according to the UL-94 test. Developing sustainable composites that are chemically synthesized from renewable sources is important from the aspect of preserving the environment and existing resources as well as the extending their life cycle.

This study investigates the surface properties of bio-based unsaturated polyester resin (b-UPR) nanocomposites reinforced with biosilica nanoparticles derived from rice husk. The b-UPR matrix was synthesized from recycled polyethylene terephthalate (PET) and renewable monomers, providing a sustainable alternative to conventional polyester resins. Unmodified and modified biosilica particles with silanes: (3-trimethoxysilylpropyl methacrylate—MEMO, trimethoxyvinylsilane—VYNIL, and 3-aminopropyltrimethoxysilane with biodiesel—AMBD) were incorporated in different amounts to evaluate their influence on the wettability, topography, and viscoelastic behavior of the composites. Contact angle measurements revealed that the addition of modified biosilica significantly improved the hydrophobicity of the b-UPR surface. The greatest increase in the wetting angle, amounting to 79.9% compared to composites with unmodified silica, was observed in the composites containing 5 wt.% SiO₂-AMBD. Atomic force microscopy (AFM) analysis indicated enhanced surface roughness and uniform dispersion of the nanoparticles. For the composite containing 1 wt.% of silica particles, the surface roughness increased by 25.5% with the AMBD modification and by 84.2% with the MEMO modification, compared to the unmodified system. Creep testing demonstrated that the reinforced nanocomposites exhibited improved dimensional stability under sustained load compared to the neat resin. These findings confirm that the integration of surface-modified biosilica not only enhances the mechanical properties but also optimizes the surface characteristics of bio-based polyester composites, broadening their potential for high-performance and sustainable applications.