An actuator driven by moisture gradients has been developed from a homogeneous graphene oxide film, relying on the in situ formation of a bilayer structure induced by water adsorption. This actuator shows efficient and controllable bending motions, coupled with the capability of lifting objects 8 times heavier than itself.

2D metal nanomaterials offer exciting prospects in terms of their properties and functions. However, the ambient aqueous synthesis of atomically‐thin, 2D metallic nanomaterials represents a significant challenge. Herein, freestanding and atomically‐thin gold nanosheets with a thickness of only 0.47 nm (two atomic layers thick) are synthesized via a one‐step aqueous approach at 20 °C, using methyl orange as a confining agent. Owing to the high surface‐area‐to‐volume ratio, abundance of unsaturated atoms exposed on the surface and large interfacial areas arising from their ultrathin 2D nature, the as‐prepared Au nanosheets demonstrate excellent catalysis performance in the model reaction of 4‐nitrophenol reduction, and remarkable peroxidase‐mimicking activity, which enables a highly sensitive colorimetric sensing of H₂O₂ with a detection limit of 0.11 × 10⁻⁶ m. This work represents the first fabrication of freestanding 2D gold with a sub‐nanometer thickness, opens up an innovative pathway toward atomically‐thin metal nanomaterials that can serve as model systems for inspiring fundamental advances in materials science, and holds potential across a wide region of applications.

Carbonaceous nanotubes (CTs) represent one of the most popular and effective carbon electrode materials for supercapacitors, but the electrochemistry performance of CTs is largely limited by their relatively low specific surface area, insufficient usage of intratube cavity, low content of heteroatom, and poor porosity. An emerging strategy for circumventing these issues is to design novel porous CT‐based nanostructures. Herein, a spheres‐in‐tube nanostructure with hierarchical porosity is successfully engineered, by encapsulating heteroatom‐doping hollow carbon spheres into one carbonaceous nanotube (HCSs@CT). This intriguing nanoarchitecture integrates the merits of large specific surface area, good porosity, and high content of heteroatoms, which synergistically facilitates the transportation and exchange of ions and electrons. Accordingly, the as‐prepared HCSs@CTs possess outstanding performances as electrode materials of supercapacitors, including superior capacitance to that of CTs, HCSs, and their mixtures, coupled with excellent cycling life, demonstrating great potential for applications in energy storage.

Gold nanorods (AuNRs) can be synthesised with different sizes but similar aspect ratios and therefore similar surface plasmon resonances (SPRs). Their strong optical absorbance governed by their SPRs facilitates their ability to be used as molecular-targeted contrast agents for photoacoustic (PA) imaging. The size of AuNRs has an effect on the PA conversion efficiency, melting threshold, and cytotoxicity, indicating that size can have a significant impact on overall biomedical efficacy. We investigated these factors for four different AuNRs (widths of 10, 25, 40 and 50 nm) all with SPRs of 815 ± 26 nm. A size-dependent linear relationship between fluence and PA amplitude was observed, along with particle melting. Reshaping was confirmed via transmission electron microscopy and spectrophotometry at a laser fluence of 11 ± 1.7 mJ cm⁻², 20 ± 2.2 mJ cm⁻², and 40 ± 2.6 mJ cm⁻². Cytotoxicity was tested on lung cancer cells (A549) via a colourimetric assay at a maximum concentration of 3 × 10¹⁰ NP ml⁻¹. Results demonstrate the 40 nm and 50 nm AuNRs produced the highest signal for equivalent particle numbers, but displayed the highest toxicity. Conversely, the 10 nm AuNRs were the most efficient photoacoustic converters, at equivalent total mass. This study demonstrates the importance of AuNR size and concentration on selection of AuNRs for their eventual clinical use.