The growing number of commercially available machines for laser deposition welding show the growing acceptance and importance of this technology for industrial applications. Their increasing usage in research and production requires process stability and user-friendly handling. A commercially available DMG MORI LT 65 3D hybrid machine used in combination with a CCD-based coaxial temperature measurement system was utilized in this work to investigate what information relating to the intensity distribution of melt pool surfaces could be appropriate to draw conclusions about process conditions. In this study it is shown how the minimal required specific energy for a stable process can be determined, and it is indicated that the evolution of a plasma plume depends on thermal energy within the base material. An estimated melt pool area—calculated by the number of pixels (NOP) with intensities larger than a fixed, predefined threshold—builds the main measure in analysing images from the process camera. The melt pool area and its temporal variance can also serve as an indicator for an increased working distance.

In recent years, the demand for highly integrated and lightweight components has been rising sharply, especially in plastics processing. One strategy for weight-saving solutions is the development of conductive tracks and layouts directly on the polymer housing parts in order to be able to dispense with the system integration of additional printed circuit boards (PCB). This can be conducted very advantageously and flexibly with laser-based processes for functionalizing polymer surfaces. In this work, a three-step laser-based process for subsequent selective metallization is presented. Conventional injection molded components without special additives serve as the initial substrate. The Laser-Based Selective Activation (LSA) uses picosecond laser pulses to activate the plastic surface to subsequently deposit palladium. The focus is on determining the amount of deposited palladium in correlation to the laser and scan parameters. For the first time, the dependence of the metallization result on the accumulated laser fluence (F_acc) is described. The treated polymer parts are characterized using optical and scanning electron microscopy as well as a contact-type profilometer.

The laser beam polishing for glass and plastics is a purely thermal process and melts the ground or lapped structures to a depth of limited extent. This results in a smoothing of the surface, whereby the 1st - 4th order shape deviations can be corrected very well and transparent surfaces are created. The process is excellently suited for quartz glasses and other optical glasses with a low coefficient of expansion α. Furthermore, thermoplastics or metallic molds for injection molding and precision molding applications can also be polished with the laser beam. On the other hand, special measures are required for glasses with a high α, e.g. preheating of the component. For the investigations, a defocused laser beam was used for the defined preheating of glasses with high linear expansion coefficients. After reaching the material-specific preheating temperature, the laser beam was focused and the polishing process started. A defined cooling process follows again with a defocused beam. In this way, a ground biconvex lens made of boron crown glass was successfully polished. The laser-polished surfaces have an RMS value of 1- 3 nm. The polishing process can be used very flexibly. Likewise, very differently shaped optical components can be polished.The newly developed polishing regime is transferable to other optical glasses with high linear expansion coefficients.

Research and development in the field of glass-based laser additive manufacturing continues to receive significant interest within scientific and industrial contexts. In particular, powder bed fusion by laser radiation (PBF-LB) enables the additive manufacturing of porous and vitrified, complex three-dimensional components. The present study investigates the glass morphology that can be achieved using PBF-LB for components made from alkali borosilicate glass. The investigations focus on the comprehensive analysis of the entire process window, including the characterisation of porous and molten glass morphology. In particular, the influence of different laser-beam diameters, which are achieved through defocusing, and the variation in volume energy density are examined in detail and compared with conventional shaping. It was determined that the process of mechanically stable shaping is constrained to temperatures above the softening temperature and relative component densities within the range of ρrel = 37.8…94.2%. Furthermore, it has been demonstrated that the process-related line-like energy input results in the formation of characteristic vitrification strands. This research contributes to the overall understanding of the producible glass morphology and the process limitations of the PBF-LB process. In addition, the entire range of glass morphologies, ranging from open-pored to closed-melt configurations, could be analysed for the first time.

The flexible and efficient production of precise optical free-form surfaces requires advanced kinematic operating principles. Due to the complex surface geometries, polishing processes with point or linear contact are used. These generally result in longer polishing times due to the smaller footprint compared to large-area polishing tools. The creation of a high precision, polishable surface in the shaping steps of the process chain is therefore of great importance. This applies in particular to minimising the roughness, but also the depth of SSD (sub-surface damage) and the mid-spatial frequency errors before the polishing process. The article describes selected process chains for the production of free-form optics and presents options for optimising the required polishing steps.