Nowadays catalytic technologies are widely used to purify indoor and outdoor air from harmful compounds. Recently, Ag–CeO₂ composites have found various applications in catalysis due to distinctive physical-chemical properties and relatively low costs as compared to those based on other noble metals. Currently, metal–support interaction is considered the key factor that determines high catalytic performance of silver–ceria composites. Despite thorough investigations, several questions remain debating. Among such issues, there are (1) morphology and size effects of both Ag and CeO₂ particles, including their defective structure, (2) chemical and charge state of silver, (3) charge transfer between silver and ceria, (4) role of oxygen vacancies, (5) reducibility of support and the catalyst on the basis thereof. In this review, we consider recent advances and trends on the role of silver–ceria interactions in catalytic performance of Ag/CeO₂ composites in low-temperature CO oxidation, soot oxidation, and volatile organic compounds (VOCs) abatement. Promising photo- and electrocatalytic applications of Ag/CeO₂ composites are also discussed.

Alcohols (bioalcohols) is a class of chemicals that are used as a feedstock for the manufacturing of a large number of valuable intermediates in industrially important processes. Currently, sustainable technologies for selective conversion of alcohols utilize “green” oxidants, mainly, ambient air or oxygen. Due to the high affinity of oxygen towards silver, the latter serves as an active component of supported heterogeneous catalysts. In this review, we consider Ag-based catalysts that participate in gas- or liquid-phase oxidation of alcohols. Oxidation of methanol, ethanol, ethylene glycol, propylene glycol, glycerol, benzyl and allyl alcohols is mostly considered. A particular attention is paid to selective photooxidation of alcohols over Ag-based catalysts. We discuss the catalyst composition in terms of (1) the state of the active component, (2) the nature of the substrate, (3) support nature, and (4) the strength of the metal–support interactions.