Objective Preheated resins (PR) are considered a cementing agent option for indirect adhesive restorations of composite inlays and onlays. The objective of this in vitro study was to evaluate the marginal sealing, adhesive interface, and microtensile bond strength of indirect adhesive restorations of composites in terms of dentin cemented with PR. Materials and Methods Standardized Class II preparations were performed on 30 extracted human premolars, impressions were taken, and indirect composite restorations were manufactured. In total, 15 restorations were cemented with PR (ENA HRi, SYNCA), and 15 restorations were cemented with self-adhesive resinous cement (RC) (Relyx U200, 3M ESPE), followed by a thermocycling regime. After that, these were segmented sagittally and longitudinally to evaluate the marginal sealing and the adhesive interface with scanning electron microscopy and confocal microscopy. Microtensile bond strength was assessed with a mechanical device (TA. XT Plus C, Stable Micro System). Statistical analysis Statistical analysis was conducted using the two-sample Student’s t-test. Results The results showed that there is no statistically significant difference in the degree of microfiltration using PR or RC; however, microtensile bond strength is greater when the restoration is cemented with RC (278.75 N/cm³) than with PR (144.49 N/cm³), and better adjustment and sealing were observed for composite restorations with PR. Conclusion PR comprise an alternative cementing agent for indirect composite restorations in Class II cavities in premolars. Publication Date: 15 September 2020 (online) © . Thieme Medical and Scientific Publishers Private Ltd. A-12, Second Floor, Sector -2, NOIDA -201301, India

The fabrication of instructive materials to engineer bone substitute scaffolds is still a relevant challenge. Current advances in additive manufacturing techniques make possible the fabrication of 3D scaffolds with even more controlled architecture at micro- and submicrometric levels, satisfying the relevant biological and mechanical requirements for tissue engineering. In this view, integrated use of additive manufacturing techniques is proposed, by combining 3D printing and air-jet spinning techniques, to optimize the fabrication of PLA tubes with nanostructured fibrous coatings for long bone defects. The physicochemical characterization of the 3D tubular scaffolds was performed by scanning electron microscopy, thermogravimetric analysis, differential scanning calorimetry, profilometry, and mechanical properties. In vitro biocompatibility was evaluated in terms of cell adhesion, proliferation, and cell–material interactions, by using human fetal osteoblasts to validate their use as a bone growth guide. The results showed that 3D-printed scaffolds provide a 3D architecture with highly reproducible properties in terms of mechanical and thermal properties. Moreover, nanofibers are collected onto the surface, which allows forming an intricate and interconnected network that provides microretentive cues able to improve adhesion and cell growth response. Therefore, the proposed approach could be suggested to design innovative scaffolds with improved interface properties to support regeneration mechanisms in long bone treatment.