The ability to predict the grinding force for hard and brittle materials is important to optimize and control the grinding process. However, it is a difficult task to establish a comprehensive grinding force model that takes into account the brittle fracture, grinding conditions, and random distribution of the grinding wheel topography. Therefore, this study developed a new grinding force model for micro-grinding of reaction-bonded silicon carbide (RB-SiC) ceramics. First, the grinding force components and grinding trajectory were analysed based on the critical depth of rubbing, ploughing, and brittle fracture. Afterwards, the corresponding individual grain force were established and the total grinding force was derived through incorporating the single grain force with dynamic cutting grains. Finally, a series of calibration and validation experiments were conducted to obtain the empirical coefficient and verify the accuracy of the model. It was found that ploughing and fracture were the dominate removal modes, which illustrate that the force components decomposed are correct. Furthermore, the values predicted according to the proposed model are consistent with the experimental data, with the average deviation of 6.793% and 8.926% for the normal and tangential force, respectively. This suggests that the proposed model is acceptable and can be used to simulate the grinding force for RB-SiC ceramics in practice.

In this paper, nanoindentation tests of GGG single crystal are performed on an Agilent G200 nanoindenter. The surface morphology and subsurface deformation mechanism induced by the nanoindentation are analyzed by a scanning electron microscope and a transmission electron microscope (TEM), respectively. The ductile deformation mechanism of GGG single crystal induced by the nanoindentation is a combination of “polycrystalline nanocrystallites” and “amorphous transformation.” In addition, the relationships between the normal force and elastic recovery, microhardness, elastic modulus, and fracture toughness of GGG single crystal are researched. Due to the size effect caused by the tip radius of the indenter, the elastic recovery rate and fracture toughness decrease first and then tend to be stable as the normal force increases, while the microhardness and elastic modulus increase first and then decrease to be stable as the normal force increases. The stress–strain curve of GGG single crystal is developed by using the nanoindentation test with a spherical indenter. When GGG single crystal deforms from the elastic regime into the ductile regime, the original single crystal is changed into “polycrystalline nanocrystallites” and “amorphous transformation” structures verified by TEM. Therefore, the material strength decreases, which results in a discontinuity of the stress–strain curve for GGG single crystal.

Continuous polishing is the first choice for machining optical elements with a large aperture. The lubrication in the continuous polishing is an important factor affecting the surface quality of the optical elements. In this study, the lubrication system between the optic element and polishing lap was analyzed firstly and then was verified by the measurement experiment of the friction coefficient. In addition, the numerical simulation model of the mixture lubrication was established. The polishing pressure distribution and material removal distribution can be obtained by the model. The influences of the rotating speed, optical element load, and surface roughness of the polishing lap on polishing pressure were also analyzed. Finally, the influence rules of the lubrication on the surface shape of optical elements were revealed by the polishing experiments.

Potassium dihydrogen phosphate (KDP) crystals, vital for high-power laser systems, pose significant machining challenges due to their brittleness, low hardness, and hygroscopic properties. Achieving crack-free, high-precision surfaces is essential but complex. Single-point diamond fly-cutting (SPDF) is the primary method, yet it exposes tools to high mechanical stress and heat, accelerating wear. In dry cutting, worn tools develop adhesive layers that detach, causing scratches and degrading surface quality. Traditional wet cutting improves surface finish but leaves residual fluids that contaminate the surface with metal ions, leading to optical degradation and fogging. To address these issues, this study explores mixed-fat-based minimum quantity lubrication (MQL) as a sustainable alternative, comparing two lubricants: biodegradable-base mixed ester lubrication (BBMEL) and hydrocarbon-based synthetic lubricant (HCBSL). A comprehensive evaluation method was developed to analyze surface roughness, tool wear, and subsurface damage under dry cutting, MQL-BBMEL, and MQL-HCBSL conditions. Experimental results show that MQL-BBMEL significantly enhances machining performance, reducing average surface roughness by 27.77% (Sa) and 44.77% (Sq) and decreasing tool wear by 25.16% compared to dry cutting, outperforming MQL-HCBSL. This improvement is attributed to BBMEL’s lower viscosity and higher proportion of polar functional groups, which form stable lubricating films, minimizing friction and thermal effects. Structural analyses confirm that MQL-BBMEL prevents KDP crystal deliquescence and surface fogging. These findings establish MQL-BBMEL as an eco-friendly, high-performance solution for machining brittle optical materials, offering significant advancements in precision machining for high-power laser systems.