Zirconium nitride (ZrN) thin films were deposited by reactive RF magnetron sputtering on Ti-6Al-4V and Si (100) substrates for potential use in biomedical applications. The tribological behaviour was evaluated against bovine bone in dry condition using a pin-on-disc apparatus. Abrasion is the primary wear mechanism observed in ZrN/bone contact. The corrosion properties were determined through two electrochemical techniques: potentiodynamic polarization and electrochemical impedance spectroscopy. The coatings with reduced oxygen content provided: (i) good resistance against corrosion when exposed to physiological solution and (ii) better anti-bioadhesion against Staphylococcus aureus bacteria.

Cr–Zr–N films have been synthesised using R.F reactive magnetron sputtering system on Si (100) wafer and XC100 steel substrate without heating. The structural, mechanical and friction coefficient evolution as a function of the Zr content were investigated by XRD, (EDS, WDS), WPS, XPS, SEM, AFM, nanoindentation, Scratch adhesion and pin-on-disc sliding wear tests. The results show, that, with increasing Zr content, the film structure changed with the coexistence of (Cr–N, Zr–N) crystallographic orientation mixture. The films formed a (Cr, Zr) N solid solution where Zr atoms substitute Cr atoms. CrN lattice parameter increased from 4.17 to 4.32 Å with the crystallite size refinement. The mechanical parameters (H, σ, E, H/E and H³/E²) were significantly improved in comparison to binary films, especially at 29 at.-% Zr. The friction and wear behaviour of the Cr–Zr (29 at.-% Zr)–N coating also showed a significant improvement.