In this study, the change in microstructure and microhardness adjacent to the tool during the friction stir processing (FSP) of 6061-T6 extrusions was investigated. Results showed that the as-received extrusions contained Fe-rich constituent particles with two distinct size distributions: coarse particles in bands and finer particles in the matrix. After FSP, Fe-containing particles exhibited single-size distribution and the coarse particles appeared to be completely eliminated through refinement. Microhardness tests showed the presence of four distinct zones and that hardness increased progressively from the dynamically recrystallized closest to the tool, outward through two distinct zones to the base material. The similarities and differences between the results of this study and others in the literature are discussed in detail.

The diameter of a H13 steel tool with M6 threads and a pin diameter of 5.9 mm and a pin length of 5 mm was measured after each 25.4 mm length of friction stir processing (FSP) of 6061-T6 extrusions. The change in pin diameter with FSP time or distance did not exhibit any steady state and was found to have two distinct regions. Metallographic analysis of two tools subjected to FSP for 60 and 120 seconds showed that (i) threads fractured in early stages of FSP, (ii) a built-up layer formed between the threads, and (iii) threads progressively wore with processing time. The metallographic analysis of an embedded tool showed the presence of a fractured piece of the tool in the stir zone. These points are discussed in detail in the paper.