One of the most common loading conditions that bonded joints experience in service is repeated impact. Despite the destructive effects of impact fatigue, the behavior of metal-composite bonded joints subjected to repeated impact loads has rarely been studied in the literature. Therefore, it is of utmost importance to pay attention to this phenomenon on the one hand and to find solutions to improve the impact fatigue life of bonded composite metal components on the other hand. Accordingly, in this study, the use of the bi-adhesive technique is proposed to improve the durability of composite-metal single-lap joints (SLJs) under impact fatigue loading conditions. J-N (energy-life) method is also used to analyze the experimental data obtained. Accordingly, in the present study, the impact fatigue behavior of single adhesive metal to composite joints was analyzed experimentally based on the J-N method and also numerically using the finite element method (FEM). By using two adhesives along a single overlap, the impact fatigue life of joints between dissimilar composite and metal joints was also analyzed experimentally. The results show that the double adhesives technique can significantly improve the impact fatigue life of the tested joints. It was also found that the optimum length ratio of the adhesives (the length covered by the ductile adhesive relative to the total overlap size) is a function of the stiffness of the joint and is more pronounced for less stiff bonded joints. A linear elastic numerical analysis was also conducted to evaluate the stress state along the bloodline of the bonded joints. Results show that the compressive peel stress made at the boundary of the two adhesives can be a possible reason behind the different results observed.

Friction stir welding (FSW) is a solid-state welding process capable of joining a wide range of light metals. However, liquation and solidification may occur during joining of dissimilar metals which leads to eutectic formation. This article aims to discover the influence of tool rotation speed on the formation of eutectic structure during friction stir welding of aluminum to magnesium. To do so, friction stir welding was performed at 600 and 950 rpm to join pure aluminum and ECO-AZ91 magnesium alloy in a lap configuration. In order to investigate the influence of the welding speed, the welding speeds of 23.5 and 37.5 mm/min were also chosen. Scanning electron microscopy (SEM) was used to study the microstructure of the joints. A shear-tensile test was used to evaluate the joints’ strengths. The fracture surfaces were also studied by SEM. The results revealed that changing the rotation speed directly affects the eutectic formation, whereas the welding speed had no influence. A lower rotation speed resulted in a thin, continuous intermetallic layer, whereas a higher speed led to the formation of a massive Mg-Al₁₂Mg₁₇ eutectic microstructure. The formation of eutectic, as an indicative of liquation, may affect the material flow during the process due to decreasing the friction coefficient between the tool and material. The macrostructure analyses showed that the phase evolution as well as the mechanism of material flow are highly affected by liquation.

This paper introduces a new model for prediction of tensile properties of Al A357 castings in the form of UTS (MPa) = a + b ln (G/√Ṫ) and El (%) = c + d ln (G/√Ṫ). While previous models use only SDAS for prediction of tensile properties of the castings, the present model uses G (temperature gradient at solidification front) to evaluate the difficulty of liquid metal feeding and formation of microshrinkages and Ṫ (cooling rate of solidifying alloy) to provide information about SDAS. The proposed model has been developed based on the data from a series of defect free plates and later was applied for prediction of tensile properties of new castings from A357 alloy. It was found that the model successfully predicts the tensile properties of cast Al A357 alloys.