This article reports the two-step synthesis of NiFeO_x nanomaterials and their characterization and bifunctional electrocatalytic activity measurements in alkaline electrolyte for metal-air batteries. The samples were mostly in layered double hydroxide at the initial temperature, but upon heat treatment, they were converted to NiFe₂O₄ phases. The electrochemical behaviour of the different samples was studied by linear sweep voltammetry and cyclic voltammetry on the glassy carbon electrode. The OER catalyst activity was observed for low mass loadings (0.125 mg cm⁻²), whereas high catalyst loading exhibited the best performance on the ORR side. The sample heat-treated at 250 °C delivered the highest bi-functional oxygen evolution and reduction reaction activity (OER/ORR) thanks to its thin-holey nanosheet-like structure with higher nickel oxidation state at 250 °C. This work further helps to develop low-cost electrocatalyst development for metal-air batteries.

In this work, we have studied a 2% copper substituted core shell type iron/iron carbide as a negative electrode for application in energy storage. The NanoFe-Fe₃C-Cu delivered 367 mAh g⁻¹ at ≈80% current efficiency, successfully running for over 300 cycles. The superior electrode kinetics and performance were assessed by rate capability, galvanostatic, potentiodynamic polarization measurements in 6 M KOH electrolyte and at ambient temperature. Ex-situ XRD characterizations and SEM images of both the fresh and used electrode surfaces show that nanoparticles were found to be still intact with negligible particle agglomeration. The electrodes have shown stable performances with low capacity decay, whereas sulfur dissolution from the additive Bi₂S₃ was found to decrease the charging efficiency with time. This core-shell type structured nano material is, consequently, an auspicious anode candidate in alkaline-metal/air and Ni-Fe battery systems.

Non-precious metal bifunctional catalysts are of great interest for metal–air batteries, electrolysis, and regenerative fuel cell systems due to their performance and cost benefits compared to the Pt group metals (PGM). In this work, metal oxides of La_0.1Ca_0.9MnO₃ and nano Co₃O₄₇ catalyst as bifunctional catalysts were used in oxygen reduction and evolution reactions (ORER). The catalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and N₂ adsorption isotherms. The electrocatalytic activity of the perovskite-type La_0.1Ca_0.9MnO₃ and Co₃O₄ catalysts both as single and mixtures of both were assessed in alkaline solutions at room temperature. Electrocatalyst activity, stability, and electrode kinetics were studied using cyclic voltammetry (CV) and rotating disk electrode (RDE). This study shows that the bifunctional performance of the mixed La_0.1Ca_0.9MnO₃ and nano Co₃O₄ was superior in comparison to either La_0.1Ca_0.9MnO₃ or nano Co₃O₄ alone for ORER_. The improved activity is due to the synergistic effect between the La_0.1Ca_0.9MnO₃ and nano Co₃O₄ structural and surface properties. This work illustrates that hybridization between these two metal oxides results in the excellent bifunctional oxygen redox activity, stability, and cyclability, leading to a cost-effective application in energy conversion and storage, albeit to the cost of higher catalyst loadings.

A facile synthesis of 3d-metal based electro-catalysts directly incorporated into a carbon support was carried out by γ-radiation. Transition metals of period 4, i.e. Ni and Co, were precipitated and reduced from their respective salt solutions. The obtained materials were characterized by XRD, SEM, SQUID and the BET methods. Thereafter, the electrodes for fuel cells were fabricated out of synthesized material and their electrochemical performance for the oxygen reduction reaction in 6 M KOH was measured. Although the concentrations of Co and Ni in the electrode material were low (3.4% Co and 0.4% Ni) after reduction by irradiation, both the Ni and Co-based gas diffusion electrodes showed high catalytic activity for oxygen reduction both at room temperature and at 60 °C.

This article reports the two-step synthesis of NiFeOx nanomaterials, their characterisation and bifunctional electrocatalytic activity measurements in alkaline electrolyte for metal-air batteries. The samples were mostly in layered double hydroxide at the initial temperature, but upon heat treatment, they were converted to NiFe2O4 phases. The electrochemical behaviour of the different samples was studied by linear sweep voltammetry and cyclic voltammetry on the glassy carbon electrode. The OER catalyst activity was observed for low mass loadings (0.125 mg cm−2), whereas high catalyst loading exhibited the best performance on the ORR side. The sample heat treated at 250 °C delivered the highest bi-functional oxygen evolution and reduction reaction activity (OER/ORR) thanks to its thin-holey nanosheet like structure with higher nickel oxidation state at 250 °C. This work further helps to develop low-cost electrocatalyst development for metal-air batteries.