New zirconia compositions with optimized esthetic properties have emerged due to the fast-growing technology in zirconia manufacturing. However, the large variety of commercial products and synthesis routes, make impossible to include all of them under the general term of "monolithic zirconia ceramics". Ultra- or high translucent monolithic formulations contain 3-8 mol% yttria, which results in materials with completely different structure, optical and mechanical properties. The purpose of this study was to provide an update to the current knowledge concerning monolithic zirconia and to review factors related to strength and aging resistance. Factors such as composition, coloring procedures, sintering method and temperature, may affect both strength and aging resistance to a more or less extend. A significant reduction of mechanical properties has been correlated to high translucent zirconia formualtions while regarding aging resistance, the findings are contradictory, necessitating more and thorough investigation. Despite the obvious advantages of contemporary monolithic zirconia ceramics, further scientific evidence is required that will eventually lead to the appropriate laboratory and clinical guidelines for their use. Until then, a safe suggestion should be to utilize high-strength partially-stabilized zirconia for posterior or long span restorations and fully-stabilized ultra-translucent zirconia for anterior single crowns and short span fixed partial dentures.

The purpose of this paper was to update the knowledge concerning the wear, translucency, as well as clinical performance of monolithic zirconia ceramics, aiming at highlighting their advantages and weaknesses through data presented in recent literature. New ultra-translucent and multicolor monolithic zirconia ceramics present considerably improved aesthetics and translucency, which, according to the literature reviewed, is similar to those of the more translucent lithium disilicate ceramics. A profound advantage is their high strength at thin geometries preserving their mechanical integrity. Based on the reviewed articles, monolithic zirconia ceramics cause minimal wear of antagonists, especially if appropriately polished, although no evidence still exists regarding the ultra-translucent compositions. Concerning the survival of monolithic zirconia restorations, the present review demonstrates the findings of the existing short-term studies, which reveal promising results after evaluating their performance for up to 5 or 7 years. Although a significant increase in translucency has been achieved, new translucent monolithic zirconia ceramics have to be further evaluated both in vitro and in vivo for their long-term potential to preserve their outstanding properties. Due to limited studies evaluating the wear properties of ultra-translucent material, no sound conclusions can be made, whereas well-designed clinical studies are urgently needed to enlighten issues of prognosis and long-term survival.

In a century when environmental pollution is a major issue, polymers issued from bio-based monomers have gained important interest, as they are expected to be environment-friendly, and biocompatible, with non-toxic degradation products. In parallel, hyperbranched polymers have emerged as an easily accessible alternative to dendrimers with numerous potential applications. Glycerol (Gly) is a natural, low-cost, trifunctional monomer, with a production expected to grow significantly, and thus an excellent candidate for the synthesis of hyperbranched polyesters for pharmaceutical and biomedical applications. In the present article, we review the synthesis, properties, and applications of glycerol polyesters of aliphatic dicarboxylic acids (from succinic to sebacic acids) as well as the copolymers of glycerol or hyperbranched polyglycerol with poly(lactic acid) and poly(ε-caprolactone). Emphasis was given to summarize the synthetic procedures (monomer molar ratio, used catalysts, temperatures, etc.,) and their effect on the molecular weight, solubility, and thermal and mechanical properties of the prepared hyperbranched polymers. Their applications in pharmaceutical technology as drug carries and in biomedical applications focusing on regenerative medicine are highlighted.

Mesoporous silica-based nanoparticles (MSNs) are considered promising drug carriers because of their ordered pore structure, which permits high drug loading and release capacity. The dissolution of Si and Ca from MSNs can trigger osteogenic differentiation of stem cells towards extracellular matrix calcification, while Mg and Sr constitute key elements of bone biology and metabolism. The aim of this study was the synthesis and characterization of sol–gel-derived MSNs co-doped with Ca, Mg and Sr. Their physico-chemical properties were investigated by X-ray diffraction (XRD), scanning electron microscopy with energy dispersive X-ray analysis (SEM/EDX), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), X-ray fluorescence spectroscopy (XRF), Brunauer Emmett Teller and Brunauer Joyner Halenda (BET/BJH), dynamic light scattering (DLS) and ζ-potential measurements. Moxifloxacin loading and release profiles were assessed with high performance liquid chromatography (HPLC) cell viability on human periodontal ligament fibroblasts and their hemolytic activity in contact with human red blood cells (RBCs) at various concentrations were also investigated. Doped MSNs generally retained their textural characteristics, while different compositions affected particle size, hemolytic activity and moxifloxacin loading/release profiles. All co-doped MSNs revealed the formation of hydroxycarbonate apatite on their surface after immersion in simulated body fluid (SBF) and promoted mitochondrial activity and cell proliferation.

Background: One type of failure in complete or partial dentures is the detachment of resin teeth from denture base resin (DBR). This common complication is also observed in the new generation of digitally fabricated dentures. The purpose of this review was to provide an update on the adhesion of artificial teeth to denture resin substrates fabricated by conventional and digital methods. Methods: A search strategy was applied to retrieve relevant studies in PubMed and Scopus. Results: Chemical (monomers, ethyl acetone, conditioning liquids, adhesive agents, etc.) and mechanical (grinding, laser, sandblasting, etc.) treatments are commonly used by technicians to improve denture teeth retention with controversial benefits. Better performance in conventional dentures is realized for certain combinations of DBR materials and denture teeth after mechanical or chemical treatment. Conclusions: The incompatibility of certain materials and lack of copolymerization are the main reasons for failure. Due to the emerging field of new techniques for denture fabrication, different materials have been developed, and further research is needed to elaborate the best combination of teeth and DBRs. Lower bond strength and suboptimal failure modes have been related to 3D-printed combinations of teeth and DBRs, while milled and conventional combinations seem to be a safer choice until further improvements in printing technologies are developed.

(1) Background: An element that has gained much attention in industrial and biomedical fields is Cerium (Ce). CeO₂ nanoparticles have been proven to be promising regarding their different biomedical applications for the control of infection and inflammation. The aim of the present study was to investigate the biological properties and antimicrobial behavior of cerium oxide (CeO₂) nanoparticles (NPs). (2) Methods: The investigation of the NPs’ biocompatibility with human periodontal ligament cells (hPDLCs) was evaluated via the MTT assay. Measurement of alkaline phosphatase (ALP) levels and alizarine red staining (ARS) were used as markers in the investigation of CeO₂ NPs’ capacity to induce the osteogenic differentiation of hPDLCs. Induced inflammatory stress conditions were applied to hPDLCs with H₂O₂ to estimate the influence of CeO₂ NPs on the viability of cells under these conditions, as well as to reveal any ROS scavenging properties. Total antioxidant capacity (TAC) of cell lysates with NPs was also investigated. Finally, the macro broth dilution method was the method of choice for checking the antibacterial capacity of CeO₂ against the anaerobic pathogens Porphyromonas gingivalis and Prevotella intermedia. (3) Results: Cell viability assay indicated that hPDLCs increase their proliferation rate in a time-dependent manner in the presence of CeO₂ NPs. ALP and ARS measurements showed that CeO₂ NPs can promote the osteogenic differentiation of hPDLCs. In addition, the MTT assay and ROS determination demonstrated some interesting results concerning the viability of cells under oxidative stress conditions and, respectively, the capability of NPs to decrease free radical levels over the course of time. Antimicrobial toxicity was observed mainly against P. gingivalis. (4) Conclusions: CeO₂ NPs could provide an excellent choice for use in clinical practices as they could prohibit bacterial proliferation and control inflammatory conditions.