The Ni-Fe coatings modified with AuNPs were deposited on the flexible copper-coated polyimide (Cu/PI) surface using electroless metal plating, while the galvanic displacement technique was applied to modify the surface of NiFe coatings by a small content of AuNPs in the range of 16.5 µg_Au cm⁻². AuNPs of a few nanometers in size were deposited on the NiFe/Cu/PI surface by immersing it in a solution containing AuCl₄⁻ ions. The electrooxidation of sodium borohydride was evaluated in a 1 M NaOH solution containing 0.05 M of sodium borohydride using cyclic voltammetry, chronoamperometry, and chronopotentiometry. In addition, the performance and stability of the NiFe/Cu/PI and AuNPs-NiFe/Cu/PI catalysts were evaluated for potential use in a direct NaBH₄-H₂O₂ fuel cell. The NiFe coating modified with AuNPs demonstrated significantly higher electrocatalytic activity towards the oxidation of sodium borohydride as compared to bare Au or unmodified NiFe/Cu/PI. Furthermore, it exhibited a superior power density of 89.7 mW cm⁻² at room temperature and operational stability under alkaline conditions, while the NiFe anode exhibited 73.1 mW cm⁻². These results suggest that the AuNPs-modified NiFe coating has great potential as a material for use in direct borohydride fuel cells (DBFCs) applications involving the oxidation of sodium borohydride.