Concrete is a brittle material due to its poor tensile strength; consequently, concrete tends to crack or peel under an applied external load. Previous studies have investigated the effect of incorporating fiber into concrete, which can improve its tensile strength. In this study, the static and dynamic mechanical characteristics of three types of fiber-reinforced concrete (FRC) were examined: carbon-fiber-reinforced concrete (CFRC); Kevlar-fiber-reinforced concrete (KFRC); and a combination of both, known as carbon/Kevlar-hybrid-fiber-reinforced concrete (HFRC). This study created concrete specimens by pneumatically dispersing carbon and Kevlar fibers and mixing them with cement to comprise 1% of the weight. The mixture was then combined with aggregates and water to form the concrete specimens. When compared with the benchmark concrete specimens, it was found that the compressive strength of the CFRC, KFRC, and HFRC specimens increased by about 19% to 50%, the bending strength increase by about 8% to 32%, and the splitting strength increased by about 4% to 36%. Specifically, the HFRC made with the 24 mm carbon and Kevlar fibers displayed the most significant mechanical strength in a static state. Furthermore, the HFRC showed superior resistance to impact compared to the benchmark concrete specimens across various impact energies, with the 24 mm carbon and Kevlar fiber HFRC showing the highest resistance. The inclusion of fibers in the split Hopkinson pressure bar (SHPB) test demonstrated a notable increase in the maximum strength, particularly in the case of the 12 mm carbon fiber combined with the 24 mm Kevlar fiber in the HFRC specimen.

In this study, comprehensive analyses were used to evaluate the physical and chemical properties of basalt fibers, employing a variety of instruments. Additionally, heat treatment and solvent treatment methods were used to eliminate the sizing present on fiber surfaces. The heat treatment process involved determining the optimal temperature and duration required to remove the sizing from the basalt fibers. The appearance, chemical composition, and crystal structure of the original fibers were examined, including those subjected to heat treatment and those treated with solvents. These treated fibers were then incorporated into concrete to create basalt fiber-reinforced concrete (BFRC) specimens for mechanical tests, which assessed their compressive, flexural, and splitting tensile strengths. The results revealed that heat treatment at 300 °C for 180 min effectively removed the sizing on the basalt fibers, and the heat-treated basalt fibers exhibited uniform dispersion inside the BFRC specimens. In addition, solvent treatment primarily removed the soluble components of the sizing. The mechanical properties of specimens with sizing-removed basalt fibers were better than the specimens with original basalt fibers and the benchmark specimens. Crucially, the mechanical test results demonstrated that BFRC incorporating heat-treated basalt fibers exhibited a superior mechanical performance compared to BFRC incorporating original fibers or fibers subjected to the solvent treatment.