In this paper, water-soluble 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO)-oxidized cellulose with a high degree of oxidation was prepared by a two-step process using bamboo dissolving pulp. The first step was to destroy the cellulose crystal I by NaOH/urea solution to obtain cellulose powder with decreased crystallinity. The second step was to oxidize the cellulose powder by TEMPO oxidation. The TEMPO-oxidized cellulose was analyzed by Fourier transform infrared spectroscopy (FTIR), conductimetry, X-ray diffraction (XRD), fiber analyzer, and transmission electron microscopy (TEM). FTIR showed that the hydroxymethyl groups in cellulose chains were converted into carboxyl groups. The degree of oxidation measured by conductimetry titration was as high as 91.0%. The TEMPO-oxidized cellulose was soluble in water for valuable polyelectrolytes and intermediates.

Self-healing gels based on reshuffling disulfide bonds have attracted great attention due to their ability to restore structure and mechanical properties after damage. In this work, self-healing gels with different cellulose nanocrystals (CNC) contents were prepared by embedding the thiuram disulfide bonds into gels via polyaddition. By the reshuffling of thiuram disulfide bonds, the CNC-containing gels repair the crack and recover mechanical properties rapidly under visible light in air. The thiuram disulfide-functionalized gels with a CNC content of 2.2% are highly stretchable and can be stretched approximately 42.6 times of their original length. Our results provide useful approaches for the preparation of dynamic CNC-containing gels with implications in many related engineering applications.