Laser shock processing (LSP) is a surface treatment technique used to enhance mechanical properties such as hardness, corrosion resistance, and wear resistance. This study investigates the effects of LSP on a 6061-T6 aluminium alloy using four treatment conditions: nanosecond (ns-LSP), picosecond (ps-LSP), and a combination of nanosecond–picosecond (nsps-LSP) and picosecond–nanosecond (psns-LSP) pulses. Two laser systems were employed: a Q-switched Nd:YAG laser (850 mJ/pulse, 6 ns, 1064 nm, 10 Hz), and an Ekspla Atlantic 355-60 laser (0.110 mJ/pulse, 13 ps, 1064 nm, 1 kHz). All treatments induced compressive residual stresses up to 1 mm in depth. Additionally, improvements in microhardness were observed, particularly at deeper layers in the combined nsps-LSP treatment. Surface roughness was measured and compared. Among all configurations, the nsps-LSP treatment produced the highest compressive residual stresses (−428 MPa) and greater microhardness at depth. These results suggest that the combined nsps-LSP treatment represents a promising approach to enhance the mechanical performance of metallic components.

Laser shock peening (LSP) is a surface treatment technique focused on improving the mechanical performance of metal components by inducing compressive residual stresses. This research evaluated the effects of LSP on a Ti-6Al-4V alloy, an α + β titanium alloy manufactured by wrought and additive manufacturing used in biomedical and aerospace applications. Samples manufactured by conventional processes and additive manufacturing were treated under the following conditions: Pulse width of 6 ns, wavelength of 1064 nm, scan density of 2500 pulses/cm², pulse energy of 0.750 J, and repetition frequency of 10 Hz. The mechanical response was evaluated in terms of residual stress, microhardness, and microstructure before and after treatment. The results showed significant improvements, reaching compressive residual stress fields of up to −800 MPa and a 22% increase in microhardness, and grain refinement from 18.16 μm to 5.54 μm. These results confirm the effectiveness of LSP in improving the surface integrity and mechanical behavior of Ti64 components, regardless of their manufacturing method.

Laser shock processing (LSP) is a surface treatment technique used to enhance mechanical properties such as hardness, corrosion resistance, and wear resistance. This study investigates the effects of LSP on a 6061-T6 aluminium alloy using four treatment conditions: nanosecond (ns-LSP), picosecond (ps-LSP), and a combination of nanosecond-picosecond (nsps-LSP) and picosecond-nanosecond (psns-LSP) pulses. Two laser systems were employed: a Q-switched Nd:YAG laser (850 mJ/pulse, 6 ns, 1064 nm, 10 Hz), and an Ekspla Atlantic 355-60 laser (0.110 mJ/pulse, 13 ps, 1064 nm, 1 kHz). All treatments induced compressive residual stresses up to 1 mm in depth. Additionally, improvements in microhardness were observed, particularly at deeper layers in the combined nsps-LSP treatment. Surface roughness was measured and compared. Among all configurations, the nsps-LSP treatment produced the highest compressive residual stresses (428 MPa) and greater microhardness at depth. These results suggest that the combined nsps-LSP treatment represents a promising approach to enhance the mechanical performance of metallic components.