In this work, we examined the influence of different types of selective laser melting (SLM) devices on the microstructure and the associated material properties of austenitic 316L stainless steel. Specimens were built using powder from the same powder batch on four different SLM machines. For the specimen build-up, optimized parameter sets were used, as provided by the manufacturers for each individual SLM machine. The resulting microstructure was investigated by means of scanning electron microscopy, which revealed that the different samples possess similar microstructures. Differences between the microstructures were found in terms of porosity, which significantly influences the material properties. Additionally, the build-up direction of the specimens was found to have a strong influence on the mechanical properties. Thus, the defect density defines the material’s properties so that the ascertained characteristic values were used to determine a Weibull modulus for the corresponding values in dependence on the build-up direction. Based on these findings, characteristic averages of the mechanical properties were determined for the SLM-manufactured samples, which can subsequently be used as reference parameters for designing industrially manufactured components.

This article reports about nanocomposites, which refractive index is tuned by adding TiO₂ nanoparticles. We compare in situ/ex situ preparation of nanocomposites. Preparation procedure is described, properties of nanocomposites are compared, and especially we examine the applicability of two-photon polymerization (2PP) of synthesized nanocomposites. All prepared samples exhibit suitable optical transparency at specific laser wavelengths. Three-dimensional structures were generated by means of two-photon polymerization effect induced by a femtosecond laser.

The use of acoustic levitation in the fields of analytical chemistry and in the containerless processing of materials requires a good stability of the levitated particle. However, spontaneous oscillations and rotation of the levitated particle have been reported in literature, which can reduce the applicability of the acoustic levitation technique. Aiming to reduce the particle oscillations, this paper presents the analysis of the particle stability in a new acoustic levitator device. The new acoustic levitator consists of a piezoelectric transducer with a concave radiating surface and a concave reflector. The analysis is conducted by determining numerically the axial and lateral forces that act on the levitated object and by measuring the oscillations of a sphere particle by a laser Doppler vibrometer. It is shown that the new levitator design allows to increase the lateral forces and reduce significantly the lateral oscillations of the levitated object.

Colors of crystals, pigments, metals, salt solutions and bioluminescence occur in nature due to the optical properties of electrons in atoms and molecules. However, colors can also result from interference effects on nanostructures. In contrast to artificial coloration, which are caused by well-defined regular structures, the structural colors of living organisms are often more intense and almost angle-independent. In this paper, we report the successful manufacturing of a lamellar nanostructure that mimics the ridge shape of the Morpho butterfly using a 3d-direct laser writing technique. The viewing angle dependency of the color was analyzed via a spectrometer and the structure was visualized using a scanning electron microscope. The generated nano- and micro-structures and their optical properties were comparable to those observed in the Morpho butterfly.

We report on the fabrication of an axicon by applying a two-step manufacturing process including a 1030 nm femtosecond and a 10.6 µm CO₂ laser. First, the pre-defined axicon geometry is generated by high-precision femtosecond layer-by-layer ablation. In order to meet high surface quality requirements, inevitable stipulated for optical use, the surface of the thus structured axicon is smoothened by a subsequent CO₂ laser polishing process. The finalized axicon fulfills optical quality as the surface roughness R_a is significantly reduced from 0.56 µm to 34 nm. For the evaluation of the optical quality, the axicon is placed in a measurement setup including the femtosecond laser. Comparison between the calculated Bessel beam for an ideal axicon and the quasi-Bessel beam generated and measured by the fabricated axicon reveals excellent agreement, verifying our precise manufacturing method.