Investigations of two-photon polymerization of inorganic–organic hybrid materials initiated by femtosecond Ti:sapphire laser pulses are performed. First applications of this technique for the fabrication of three-dimensional microstructures and photonic crystals in inorganic–organic hybrid polymers with a structure size down to 200 nm and a periodicity of 450 nm are discussed.

Stereolithography (SLA) is a widely used technique for the fabrication of prototypes and small series products. The main advantage of SLA and related solid freeform fabrication (SFF) techniques is their capability to fabricate parts with complex shapes with high resolution. Although the spectrum of available materials has been widened in recent years, there is still a lack of materials which can be processed with SLA on a routine basis. In this work, a micro-SLA (μSLA) system is presented which can shape a number of different photopolymers with resolutions down to 5 μ mi n thexy-plane and 10 μ mi n thez-direction. The system is capable of processing various specifically tailored photopolymers which are based on acrylate chemistry. The materials processed for this work range from hybrid sol-gel materials (ORMOCER) to photo-crosslinked elastomers and hydrogels. The elastic moduli of these materials can be tuned over several orders of magnitude and range from 0.1 MPa to 8000 MPa. The reactivity of these monomers is sufficient for achieving writing speeds up to 500 mm s−1 which is comparable to commercial SLA resins. Various test structures are presented which show the suitability of the process for fabricating parts required for applications in micro-mechanical systems as well as for applications in biomedical engineering. Using the presented system, internal channels with a diameter of 50 μm and a length of 1500 μm could be fabricated. It was also possible to manufacture a micro-mechanical system consisting of a fixed axe and a free spinning turbine wheel. (Some figures in this article are in colour only in the electronic version)

Alloying of refractory high entropy alloys (HEAs) such as MoNbTaW is usually done by vacuum arc melting (VAM) or powder metallurgy (PM) due to the high melting points of the elements. Machining to produce the final shape of parts is often needed after the PM process. Casting processes, which are often used for aerospace components (turbine blades, vanes), are not possible. Direct metal deposition (DMD) is an additive manufacturing technique used for the refurbishment of superalloy components, but generating these components from the bottom up is also of current research interest. MoNbTaW possesses high yield strength at high temperatures and could be an alternative to state-of-the-art materials. In this study, DMD of an equimolar mixture of elemental powders was performed with a pulsed Nd:YAG laser. Single wall structures were built, deposition strategies developed and the microstructure of MoNbTaW was analyzed by back scattered electrons (BSE) and energy dispersive X-ray (EDX) spectroscopy in a scanning electron microscope. DMD enables the generation of composition gradients by using dynamic powder mixing instead of pre-alloyed powders. However, the simultaneous handling of several elemental or pre-alloyed powders brings new challenges to the deposition process. The influence of thermal properties, melting point and vapor pressure on the deposition process and chemical composition will be discussed