Chronic wounds have become one of the most important issues for healthcare systems and are a leading cause of death worldwide. Wound dressings are necessary to facilitate wound treatment. Engineering wound dressings may substantially reduce healing time, reduce the risk of recurrent infections, and reduce the disability and costs associated. In the path of engineering of an ideal wound dressing, hydrogels have played a leading role. Hydrogels are 3D hydrophilic polymeric structures that can provide a protective barrier, mimic the native extracellular matrix (ECM), and provide a humid environment. Due to their advantages, hydrogels (with different architectural, physical, mechanical, and biological properties) have been extensively explored as wound dressing platforms. Here we describe recent studies on hydrogels for wound healing applications with a strong focus on the interplay between the fabrication method used and the architectural, mechanical, and biological performance achieved. Moreover, we review different categories of additives which can enhance wound regeneration using 3D hydrogel dressings. Hydrogel engineering for wound healing applications promises the generation of smart solutions to solve this pressing problem, enabling key functionalities such as bacterial growth inhibition, enhanced re-epithelialization, vascularization, improved recovery of the tissue functionality, and overall, accelerated and effective wound healing.

Bone defects remain a significant health issue and a major cause of morbidity in elderly patients. Composites based on collagen/calcium phosphate have been widely used for bone repair in clinical applications, owing to their comparability to bone extracellular matrix. This study aimed to evaluate the effects of a scaffold of collagen/calcium phosphate (COL/β-TCP) on bone formation to assess its potential use as a bone substitute to repair bone defects. Bilateral full-thickness critically sized calvarial defects (8 mm in diameter) were created in New Zealand white rabbits and treated with COL/β-TCP or COL scaffolds. One defect was also left unfilled as a control. Bone regeneration was assessed through histological evaluation using hematoxylin and eosin and Masson’s trichrome staining after 4 and 8 weeks. Alizarin Red staining was also utilized to observe the mineralization process. Our findings indicated that COL/β-TCP implantation could better enhance bone regeneration than COL and exhibited both new bone growth and scaffold material degradation.

Collagen (Col) type I, as the major component of the bone extracellular matrix has been broadly studied for bone tissue engineering. However,inferior mechanical properties limit its usage for load bearing applications. In this research, freeze dried Col scaffolds are coated with graphene oxide (GO) through a covalent bond of the amine Col with the graphene carboxyl groups. The prepared scaffolds were then reduced using a chemical agent. Scanning electron microscopy exhibited a porous structure for the synthesized scaffolds with an approximate pore size of 100–220 ± 12 µm, which is in the suitable range for bone tissue engineering application. Reducing the GO coating improved the compressive modulus of the Col from 250 to 970 kPa. Apatite formation was also indicated by immersing the scaffolds in simulated body fluid after five days. The cytocompatibility of the scaffolds, using human bone marrow‐derived mesenchymal stem cells, was confirmed with MTT analysis. Alkaline phosphatase assay revealed that reducing the Col–GO scaffolds can effectively activate the differentiation of hBM‐MSCs into osteoblasts after 14 days, even without the addition of an osteogenic differentiation medium. The results of this study highlight that GO and its reduced form have considerable potential as bone substitutes for orthopaedic and dental applications.