A major limitation of existing 3D implantable structures for bone tissue engineering is that most of the cells rapidly attach on the outer edges of the structure, restricting the cells penetration into the inner parts and causing the formation of a necrotic core. Furthermore, these structures generally possess a random spatial arrangement and do not preserve the isotropy on the whole volume. Here, we report on the fabrication and testing of an innovative 3D hierarchical, honeycomb-like structure (HS), with reproducible and isotropic arhitecture, that allows in ‘volume’ migration of osteoblasts. In particular, we demonstrate the possibility to control the 3D spatial cells growth inside these complex architectures by adjusting the free spaces inside the structures. The structures were made of vertical microtubes arranged in a mulitlayered configuration, fabricated via laser direct writing by two photons polymerization of the IP-L780 photopolymer. In vitro tests performed in MG-63 osteoblast-like cells demonstrated that the cells migration inside the 3D structures is conducted by the separation space between the microtubes layers. Specifically, for layers separation between 2 and 10 μ m, the cells gradually penetrated between the microtubes. Furthermore, these structures induced the strongest cells osteogenic differentiation and mineralization, with ALP activity 1.5 times stronger, amount of calcified minerals 1.3 times higher and osteocalcin secretion increased by 2.3 times compared to the other structures. On the opposite, for layers separation less than 2 μ m and above 10 μ m, the cells were not able to make interconnections and exhibited poor mineralization ability.

The design of mesoporous carbon materials with controlled textural and structural features by rapid, cost-effective and eco-friendly means is highly demanded for many fields of applications. We report herein on the fast and tailored synthesis of mesoporous carbon by UV and IR laser assisted irradiations of a solution consisting of green phenolic resins and surfactant agent. By tailoring the UV laser parameters such as energy, pulse repetition rate or exposure time carbon materials with different pore size, architecture and wall thickness were obtained. By increasing irradiation dose, the mesopore size diminishes in the favor of wall thickness while the morphology shifts from worm-like to an ordered hexagonal one. This was related to the intensification of phenolic resin cross-linking which induces the reduction of H-bonding with the template as highlighted by ¹³C and ¹H NMR. In addition, mesoporous carbon with graphitic structure was obtained by IR laser irradiation at room temperature and in very short time periods compared to the classical long thermal treatment at very high temperatures. Therefore, the carbon texture and structure can be tuned only by playing with laser parameters, without extra chemicals, as usually required.