Enhancement of membrane permeability at no detriment of its other performances, e.g., selectivity, is a goal-directed objective in membrane fabrication. A novel antioxidant DES-lignin (lignin extracted from birch wood by using a deep eutectic solvent) polyethersulfone (PES) membrane, containing 0–1 wt % DES-lignin, was fabricated with the phase inversion technique. The performance and morphology of the fabricated membranes were characterized by a pure water flux, polyethylene glycol (PEG) retention, Fourier transform infrared spectroscopy, scanning electron microscopy, and contact angle measurements. Membranes with less negative charge and better hydrophilicity were obtained when the DES-lignin content in the polymer solution was increased. With the highest dosage, the incorporation of DES-lignin in the membrane matrix improved the membrane permeability by 29.4% compared to a pure PES membrane. Moreover, no leakage of DES-lignin from the membrane structure was observed, indicating good compatibility of DES-lignin with the PES structure. It was also found that the improvement of both rejection and pure water flux could be achieved by using a small dosage of DES-lignin (0.25 wt %) in membrane fabrication. The membranes incorporated with DES-lignin showed higher DPPH (2,2-diphenyl-1-picrylhydrazyl) and ABTS (2,2-Azino-bis (3-ethylbenzothiazoline-6-sulfonic acid)) scavenging activity compared to the pure membrane, where 2.6 and 1.1 times higher DPPH and ABTS scavenging activity was observed with the highest DES-lignin content (1 wt %). Thus, the results of this study demonstrate well the feasibility of utilizing DES-lignin as an antioxidant bio-based hydrophilicity promoter in the fabrication of ultrafiltration membranes.

Fouling as an intricate process is considered as the main obstacle in membrane technologies, and its control is one of the main areas of attention in membrane processes. In this study, a commercial polyethersulfone ultrafiltration membrane (MWCO: 4000 g/mol) was surface modified with different concentrations of vanillin as an antifouling and hydrophilicity promoter to improve its performance. The presence of vanillin and its increasing adsorption potential trends in higher vanillin concentrations were clearly confirmed by observable changes in FTIR (Fourier transform infrared) spectra after modification. Membranes with better hydrophilicity (almost 30% lower contact angle in the best case) and higher polyethylene glycol solution (PEG) permeability were achieved after modification, where a 35–38% increase in permeability of aqueous solution of PEG was perceived when the membrane was modified at the highest exposure concentration of vanillin (2.8 g/L). After filtration of wood extract, surface modified membrane (2.8 g/L vanillin) showed better antifouling characteristics compared to unmodified membrane, as indicated by approximately 22% lower pure water flux reduction, which in turn improved the separation of lignin from the other organic compounds present in wood extract.

The Ni-TiO₂ and Ni-CeO₂ composite coatings with varying hydrophilic/hydrophobic characteristics were fabricated by the electrodeposition method from a tartrate electrolyte at ambient temperature. To meet the requirements of tight regulation by the European Chemicals Agency classifying H₃BO₃ as a substance of very high concern, Rochelle salt was utilized as a buffer solution instead. The novelty of this study was to implement a simple one-step galvanostatic electrodeposition from the low-temperature electrolyte based on a greener buffer compared to traditionally used, aiming to obtain new types of soft-matrix Ni, Ni-CeO₂, and Ni-TiO₂ coatings onto steel or copper substrates. The surface characteristics of electrodeposited nickel composites were evaluated by SEM, EDS, surface contact angle measurements, and XPS. Physiochemical properties of pure Ni, Ni-CeO_2, and Ni-TiO₂ composites, namely, wear resistance, microhardness, microroughness, and photocatalytic activity, were studied. Potentiodynamic polarization, EIS, and ICP-MS analyses were employed to study the long-term corrosion behavior of coatings in a 0.5 M NaCl solution. Superior photocatalytic degradation of methylene blue, 96.2% after 6 h of illumination, was achieved in the case of Ni-TiO₂ composite, while no substantial change in the photocatalytic behavior of the Ni-CeO₂ compared to pure Ni was observed. Both composites demonstrated higher hardness and wear resistance than pure Ni. This study investigates the feasibility of utilizing TiO₂ as a photocatalytic hydrophilicity promoter in the fabrication of composite coatings for various applications.

In this study cellulose-rich membranes were fabricated from untreated and treated hardwood biomass solutions in 1-ethyl-3-methylimidazolium acetate ([Emim][OAc])—dimetylsulfoxide (DMSO) system via wet phase separation. Wood treatment methods aimed to get purified cellulose fraction of wood. Treatment sequence was as followed: deep eutectic solvent pretreatment, sodium chlorite bleaching, and alkaline treatment. Resulted biomass after each treatment step was characterized by chemical composition and crystalline fraction content. Flat-sheet membranes were produced from biomass samples after each treatment step. Characterization of membranes included measurements of pure water permeability and (poly)ethyleneglycol 35 kDa retention, Fourier-transform infrared and Raman spectroscopy, X-ray diffraction measurements and thermogravimetric analysis. The study revealed that it was possible to fabricate membrane from untreated wood as well as from wood biomass after each of treatment steps. The resulted membranes differed in chemical composition and filtration performance. Membrane prepared directly from untreated wood had the highest permeability, the lowest retention; and the most complex chemical composition among others. As treatment steps removed lignin and hemicelluloses from the wood biomass, the corresponding membranes became chemically more homogeneous and showed increased retention and decreased permeability values.