Zinc molybdate (ZnMoO₄) was prepared by thermal decomposition of an oxalate complex under a controlled temperature of 500 °C. Analyses of the oxalate complex were carried out using Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). On the other hand, analyses of the synthesized zinc molybdate were carried out by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Brunauer-Emmett-Teller technique (BET). The efficiency of the synthesized catalyst was tested with the reduction reaction of 3-nitrophenol (3-NP), and was also applied as a sorbent for methylene blue dye (MB) in aqueous solutions. The catalytic test of zinc molybdate shows a very high activity. The concentration reduction progress and adsorption of the dye were followed by an ultraviolet-visible (UV-vis) spectrophotometer.

Nano Molybdenum trioxide (α-MoO₃) was synthesized in an easy and efficient approach. The removal of methylene blue (MB) in aqueous solutions was studied using this material. The effects of various experimental parameters, for example contact time, pH, temperature and initial MB concentration on removal capacity were explored. The removal of MB was significantly affected by pH and temperature and higher values resulted in increase of removal capacity of MB. The removal efficiency of Methylene blue was 100% at pH = 11 for initial dye concentrations lower than 150 ppm, with a maximum removal capacity of 152 mg/g of MB as gathered from Langmuir model. By comparing the kinetic models (pseudo first-order, pseudo second-order and intraparticle diffusion model) at various conditions, it has been found that the pseudo second-order kinetic model correlates with the experimental data well. The thermodynamic study indicated that the removal was endothermic, spontaneous and favorable. The thermal regeneration studies indicated that the removal efficiency (99%) was maintained after four cycles of use. Fourier Transform Infrared (FTIR) and Scanning Electron Microscopy (SEM) confirmed the presence of the MB dye on the α-MoO₃ nanoparticles after adsorption and regeneration. The α-MoO₃ nanosorbent showed excellent removal efficiency before and after regeneration, suggesting that it can be used as a promising adsorbent for removing Methylene blue dye from wastewater.

Waste brick materials were applied as removal materials of basic blue 41 (BB-41) from artificially contaminated water. They were characterized by different techniques prior their use. A series of removal tests were carried out at different conditions, such as a dosage effect, pH value, initial concentrations, and chemical treatment. The removal results indicated that the two untreated waste bricks had limited removal capacities of basic blue 41, ranging from 19 to 30 mg/g. However, these values were improved upon treatment with NaOH solution or by increasing the removal temperature. Waste brick collected from the Medina area (Med-WB) exhibited higher removal capacity compared to the one collected from the Jeddah area (Jed-WB), with a maximum removal capacity of 60 mg/g at 60 °C. The pH of the BB-41 solution also played an important factor, as it improved the removal amounts from 25 mg/g to 45 mg/g at initial concentration of 200 mg/L. The regenerative process was studied using oxidative reaction of the removed basic blue 41 with a solution of oxone and cobalt nitrate. The efficiency was maintained after 5 runs for Med-WB, with a slight variation of 25%, while it felt to 50% for Jed-WB material after three runs. These data indicate that the waste brick materials present as potential candidates for the dye removal and their origin has to be identified.

Removing methylene blue (MB) dye from aqueous solutions was examined by the use of nickel molybdate (α-NiMoO₄) as an adsorbent produced by an uncomplicated, rapid, and cost-effective method. Different results were produced by varying different parameters such as the pH, the adsorbent dose, the temperature, the contact time, and the initial dye concentration. Adsorbent dose and pH had a major removal effect on MB. Interestingly, a lower amount of adsorbent dose caused greater MB removal. The amount of removal gained was efficient and reached a 99% level with an initial methylene blue solution concentration of ≤160 ppm at pH 11. The kinetic studies indicated that the pseudo-second-order kinetic model relates very well with that of the obtained experimental results. The thermodynamic studies showed that removing the MB dye was favorable, spontaneous, and endothermic. Impressively, the highest quantity of removal amount of MB dye was 16,863 mg/g, as shown by the Langmuir model. The thermal regeneration tests revealed that the efficiency of removing MB (11,608 mg/g) was retained following three continuous rounds of recycled adsorbents. Adsorption of MB onto α-NiMoO₄ nanoparticles and its regeneration were confirmed by Fourier transform infrared spectroscopy (FTIR) analysis and scanning electron microscopy (SEM) analysis. The results indicated that α-NiMoO₄ nanosorbent is an outstanding and strong candidate that can be used for removing the maximum capacity of MB dye in wastewater.

Nanostructured β-CoMoO₄ catalysts have been prepared via the thermal decomposition of an oxalate precursor. The catalyst was characterized by infrared spectroscopy (FTIR), X-ray diffraction (XRD), Brunauer-Emmett-Teller method (BET), energy dispersive X-ray spectroscopy (EDX), and transmission electron microscopy (TEM). The efficiency of these nanoparticles in the reduction of ortho- and meta-nitrophenol isomers (2-NP, 3-NP, and 4-NP) to their corresponding aminophenols was tested using UV-visible spectroscopy measurements. It was found that, with a β-CoMoO₄ catalyst, NaBH₄ reduces 3-NP instantaneously, whilst the reduction of 2-NP and 4-NP is slower at 8 min. This difference is thought to arise from the lower acidity of 3-NP, where the negative charge of the phenolate could not be delocalized onto the oxygen atoms of the meta-nitro group.