2D materials with unique opto-electronic properties have shown immense potential for application in organic photovoltaics (OPVs). In this article, we reported a facile and efficient strategy to enhance the device performance of OPVs by doping 2D material of antimonene quantum sheets (AMQSs) into PEDOT:PSS emulsion. The interfacial properties between the hole extraction layer (HEL) and PBDB-T:ITIC-based active layer were properly meliorated, achieving boosted power conversion efficiency (PCE). Results indicate that the introduced AMQSs could help suppress the recombination loss and improve charge extraction efficiency. Over 8.09% enhancement of PCE is observed compared to that of the control cell with pure PEDOT:PSS. This work provides a simple and valid strategy of HEL modification to realize high efficiency OPVs.

Superhydrophobicity is the phenomenon of which the water contact angle (WCA) of droplets on a solid surface is greater than 150°. In the present paper, we prepare a superhydrophobic film with a structure similar to the surface of a lotus leaf, which is composed of polydimethylsiloxane (PDMS), zinc oxide (ZnO), a molecular sieve (MS) and 1,2,3,4,8,9,10,11,15,16,17,18,22,23,24,25-hexadecafluorophthalocyanine copper(II) (F₁₆CuPc). The F₁₆CuPc was used as the modifier to reduce the surface energy of the biomimetic micro-nanostructure. With the introduction of F₁₆CuPc, the superhydrophobic properties of the surface were enhanced so that the WCA and water roll-off angle could reach 167.1° and 0.5°, respectively. Scanning electron microscopy, X-ray energy spectrometry, and X-ray photoelectron spectroscopy analyses verified that the enhanced superhydrophobic properties of the film were mainly attributed to the modification of F₁₆CuPc. Finally, thermal, mechanical, and chemical stability studies, as well as the influences of UV and underwater immersion on the superhydrophobic film were investigated. This developed two-step fabrication method may be a potential direction for superhydrophobic surface fabrication due to its simple process, excellent superhydrophobic property, and favorable stability.