In the long-term working state, stains such as dust, oil, and charged particles in the environment are prone to deposit on the surface of the power equipment, which has great security risks. To achieve anti-stain performance, fluorocarbon composite coating with a low surface energy was prepared and studied. In this paper, SiO₂ nanoparticles were used as inorganic fillers and fluorocarbon resin was used as the substrate to form anti-stain coatings. By adjusting and optimizing the ratio of fillers and organic resins, coatings with different static contact angles were constructed. The optimum composite coating has a contact angle of 151 ± 2° and a surface energy of 9.6 mJ/m². After high-temperature treatment (up to 200 °C), immersion in corrosive solutions (pH 3–11), and sandpaper abrasion (after 5 abrasion cycles), the coating has been proven to show good thermal, chemical and mechanical stability. Our study provides significant research and market opportunities for the anti-stain application of the fluorocarbon composite coating on power equipment.

In a high-moisture environment where dust and coastal saltwater are prevalent, the stability of power equipment can be adversely affected. This issue can result in equipment downtime, particularly for transformers, severely disrupting the continuous operation of DC transmission systems. To address this challenge, a superhydrophobic modified fluorosilicone coating was developed, incorporating anti-stain properties. To tackle this issue comprehensively, an orthogonal experiment was conducted, involving six factors and three levels. The study focused particularly on assessing the impact of water-repellent recovery agents, nanofillers, antistatic agents, anti-mold agents, leveling agents, as well as wetting and dispersing agents on the coating’s surface tension. The results demonstrate that selecting an appropriate base resin and incorporating well-matched functional additives played a central role in effectively reducing the surface tension of the coating. Consequently, optimized coatings exhibited exceptional resistance to stains and displayed strong corrosion resistance.

This study focuses on formulating a low-surface-energy, water-resistant, and anti-condensation coating utilizing a fluorocarbon and acrylic resins composite (FAC), enhanced by six functional additives: antistatic agents, water-repellent agents, nanofillers, anti-mold and anti-algae agent, leveling agents, and wetting and dispersing agents. An orthogonal experimental design was implemented to systematically investigate the effects of varying concentrations of these additives on the surface tension of the coating. The results show that the optimized combination of fluorocarbon and acrylic resins composite (OFAC)with functional additives significantly reduces the surface tension, thereby improving both water resistance and anti-condensation properties. This research advances the development of more efficient surface treatment technologies, particularly for applications requiring enhanced water resistance and anti-condensation performance.

The aging tests of nitrile rubber were carried on in transformer oil, and under compression in transformer oil. The effects of compression stress on the thermal aging behaviors of nitrile rubber were studied by mechanical property measurements. The variations of physical properties during the ageing process were analyzed and compared. The change in elongation at break aging under compression stress in oil was lower than that aging in oil. The lifetime of NBR at 25˚C was predicted and compared with the compression set or elongation at break as evaluation indexes, and 50% as critical value.

Under the DC field, live contamination is more likely to deposit on the surface of insulators due to the action of the external electric field. The deposition of dirt on the surface of Ultra High Voltage (UHV) insulators can lead to the occurrence of flashover phenomena, causing significant economic losses. Due to the particularity of UHV insulators, many traditional surface anti-pollution technologies designed for normal voltage insulators are not applicable to them. In order to prevent the harm of contamination accumulation affecting the safe operation of transmission lines, in this study, tetragonal BaTiO₃ was mixed into room-temperature vulcanized silicone rubber for the first time to prepare a composite coating with piezoelectric properties. This coating can use the piezoelectric effect to remove the contamination adhering to the surface of UHV insulators under a DC field. In this study, the piezoelectric properties of the prepared tetragonal BaTiO₃ were verified through material characterization. The results show that the introduction of piezoelectric fillers can significantly accelerate the dissipation of charges on the insulator surface under slight disturbances, which helps to reduce the accumulation of charged pollutants on the insulator surface. The anti-pollution performance under electric field conditions was verified through a simulation experimental device. Finally, through experiments in a real converter station environment, the anti-pollution effect of the insulator under actual working conditions was verified.

Dissolved gas analysis (DGA) is an essential technique for the fault diagnosis and condition monitoring of oil-immersed power transformers. Among various characteristic gases, acetylene (C₂H₂) is a key indicator of high-energy discharge and arc faults. In this work, a high-sensitivity dissolved acetylene detection system is developed based on clamp-type quartz-enhanced photoacoustic spectroscopy (QEPAS). A specially designed clamp-type quartz tuning fork (Clamp-type QTF) is employed as the acoustic transducer to improve acoustic coupling efficiency and optical alignment tolerance. Compared with conventional standard quartz tuning forks, the clamp-type structure exhibits enlarged acoustic interaction volume, lower damping loss, and higher signal collection capability. A near-infrared distributed feedback (DFB) laser operating at 1531.6 nm is used as the excitation source. The dissolved gas is extracted from transformer oil using a headspace degassing module and introduced into the QEPAS cell for real-time measurement. Experimental results showed that the developed system achieves a 1σ-based SNR-estimated detection limit of 17 ppb at a 50 s integration time, derived from the continuous measurement of 0.75 ppm C₂H₂, with excellent linearity in the concentration range from 100 ppm to 500 ppm. The measured concentration of dissolved acetylene in transformer oil is in good agreement with gas chromatography (GC), validating the effectiveness and practical applicability of the proposed system.