The significant waste generated by the fashion industry necessitates sustainable textile recycling strategies. Polyester, made from poly(ethylene terephthalate) (PET), is abundant in post-consumer textiles. Technologies have been developed to convert low-density garment waste into flakes, but the role of color sorting in achieving uniform aesthetics in injection-moldable plastics remains underexplored. This study compares materials extruded from dark color-sorted polyester garment flakes with those from light-color flakes in terms of processability in extrusion and injection molding. The properties examined include melt fluidity, injection molding shrinkage, and mechanical and thermal properties. Commercial chain extenders with anhydride, oxazoline, or epoxide reactive groups were added during extrusion. Interestingly, only dark-colored extruded pellets showed significant degradation, but all the chain extenders allowed melt fluidity to be controlled during reprocessing. The bisoxazoline-based additive was the most promising, due to the highly improved ductility of the samples, regardless of whether they were dark-colored or light-colored. The results indicate significant potential for the industrial recycling of post-consumer textiles and highlight the industrial feasibility of repurposing post-consumer polyester garments. This approach not only supports initiatives of circular economy but also offers a viable solution for managing textile waste, particularly in the fashion industry. Additionally, the suggested recycling route combats the production of microplastics.

The recycling of polyamide 6 (PA) and elastane (EL) from post-consumer textiles is increasingly relevant for sustainable materials development. This study investigates blends obtained from a commercial PA fabric containing 16% EL, processed via extrusion under various conditions to evaluate the influence of temperature, screw type, and speed on phase morphology and thermo-mechanical performance. The results demonstrate that processing parameters, particularly temperature, significantly affect melt viscosity and the final mechanical properties of the blends. Enhanced ductility was observed in all recycled samples compared to pure PA, indicating that mechanical recycling is a promising strategy for PA/EL textile waste. These findings support the feasibility of this approach, while highlighting the need for further research into compatibilization techniques and industrial scalability.