The recovery and recycling of textile waste is becoming urgent since textiles are generating more and more waste. In one year, about 92 million tons of textile waste are produced and the fashion industry accounts for 58 million tons of plastic waste per year. Several different synthetic fibres are used in textiles, thanks to their excellent processability and mechanical properties, but on the other hand, the difficulties linked to their end of life and the release of microplastics from them during washing is currently a cause of great concern. In this context, policy actions have been aimed at promoting recycling of waste and replacing fossil-based fibres with biobased fibres. The current review, considering both scientific papers published on international journals and web sources, considers the sorting of textiles and the possible recycling of polyesters, polyamides and acrylics. Nevertheless, the contamination and presence of mixed fibres in fabrics is another issue to face for recycling. Methodologies to solve the issue linked to the presence of elastane, present in the stretch fabrics, as well as the possibility of recycling textiles in the non-woven and composite sector are investigated. Moreover, chemical recycling and enzymatic recycling of fossil polymers are also considered. Thanks to the comprehensive scheme of this review, it is possible to deduce that, while the use of biobased materials should rapidly increase in textile applications, the perspective of recycling materials obtained from waste textile into durable and/or high-performance products seems the most promising.

The significant waste generated by the fashion industry necessitates sustainable textile recycling strategies. Polyester, made from poly(ethylene terephthalate) (PET), is abundant in post-consumer textiles. Technologies have been developed to convert low-density garment waste into flakes, but the role of color sorting in achieving uniform aesthetics in injection-moldable plastics remains underexplored. This study compares materials extruded from dark color-sorted polyester garment flakes with those from light-color flakes in terms of processability in extrusion and injection molding. The properties examined include melt fluidity, injection molding shrinkage, and mechanical and thermal properties. Commercial chain extenders with anhydride, oxazoline, or epoxide reactive groups were added during extrusion. Interestingly, only dark-colored extruded pellets showed significant degradation, but all the chain extenders allowed melt fluidity to be controlled during reprocessing. The bisoxazoline-based additive was the most promising, due to the highly improved ductility of the samples, regardless of whether they were dark-colored or light-colored. The results indicate significant potential for the industrial recycling of post-consumer textiles and highlight the industrial feasibility of repurposing post-consumer polyester garments. This approach not only supports initiatives of circular economy but also offers a viable solution for managing textile waste, particularly in the fashion industry. Additionally, the suggested recycling route combats the production of microplastics.

For cable compound manufacturers, accurate formulation fine-tuning is essential to ensure safety, long-term durability, and compliance with international standards for dielectric strength, volume resistivity, and environmental and thermal ageing. This work presents an experimental study demonstrating how minor additives can critically affect the performance of complex flame-retardant elastomeric formulations. The investigation focuses on the role of small amounts of zinc oxide (ZnO) in commercial cable compounds based on a crosslinked elastomeric matrix composed of ethylene–propylene monomer (EPM), ethylene–propylene–diene monomer (EPDM), and thermoplastic polyolefin elastomer (POE). The formulations contain aluminium trihydroxide (ATH) as the major filler, together with several minor additives. Among these, a phenolic antioxidant (AN01) acting as a metal deactivator is also present. The addition of ZnO in low amounts (2–5 phr) allowed the compounds to maintain a volume resistivity ≥ 10¹² Ω·cm in water at 100 °C. To elucidate the role of ZnO, a systematic set of formulations was prepared by varying the type and content of selected additives. The compounds were prepared by melt mixing in an internal mixer (Banbury type), followed by peroxide crosslinking via compression molding. Electrical characterization results indicate that ZnO interacts with the phenolic additive through surface adsorption, forming a coated particle with significantly reduced electrical conductivity. Optimal electrical performance was achieved when the ZnO-to-additive ratio corresponded to the minimum amount required for complete surface complexation.

The recycling of polyamide 6 (PA) and elastane (EL) from post-consumer textiles is increasingly relevant for sustainable materials development. This study investigates blends obtained from a commercial PA fabric containing 16% EL, processed via extrusion under various conditions to evaluate the influence of temperature, screw type, and speed on phase morphology and thermo-mechanical performance. The results demonstrate that processing parameters, particularly temperature, significantly affect melt viscosity and the final mechanical properties of the blends. Enhanced ductility was observed in all recycled samples compared to pure PA, indicating that mechanical recycling is a promising strategy for PA/EL textile waste. These findings support the feasibility of this approach, while highlighting the need for further research into compatibilization techniques and industrial scalability.