Blend films of feather keratin (FK) and synthetic poly(vinyl alcohol) (PVA) that were compatibilized by tris(hydroxymethyl)aminomethane (Tris) were successfully prepared by a solution-casting method. The scanning electron microscopy (SEM) results showed that a phase separation occurred in the FK/PVA/Tris blended system. Analysis by Fourier transform infrared spectroscopy indicated that the main interactions between the three components were hydrogen bonds. In addition, X-ray diffraction analysis showed that the FK/PVA/Tris blend films were partially crystalline. The barrier properties, mechanical properties, and contact angles of the FK/PVA/Tris films were investigated to determine the effects of the PVA and Tris concentrations. More specifically, upon increasing the PVA content, the elongation at break, the hydrophilicity, and the oxygen barrier properties were enhanced. However, at a constant PVA content, an increase in the Tris content caused the oxygen permeability and the contact angle to decrease, while the tensile strength, elongation at break, and oxygen barrier properties were enhanced. These results indicated that the mechanical properties and gas resistance of the FK/PVA/Tris blend films could be successfully improved using the method described herein, confirming that this route provided a convenient and promising means to prepare FK plastics for practical applications.

In this study, feather keratin/polyvinyl alcohol/tris(hydroxymethyl)aminomethane (FK/PVA/Tris) bionanocomposite films containing two types of nanoparticles, namely one-dimensional sodium montmorillonite (MMT) clay platelets (0.5, 1, 3, and 5 wt%) and three-dimensional TiO₂ nanospheres (0.5, 1, 3, and 5 wt%), are prepared using solvent casting method. X-ray diffraction studies confirm the completely exfoliated structure of FK/PVA/Tris/MMT nanocomposites. The successful formation of new hydrogen bonds between the hydroxyl groups of the film matrix and the nanofillers is confirmed by Fourier transform infrared spectroscopy. The tensile strength, elongation at break, and initial degradation temperature of the films are enhanced after MMT and TiO₂ incorporation. The water vapor permeability, oxygen permeability, and light transmittance decrease with increase in TiO₂ and MMT contents. In summary, nanoblending is an effective method to promote the application of FK/PVA/Tris blend films in the packaging field.

In this study, feather keratin/polyvinyl alcohol/tris(hydroxymethyl)aminomethane (FK/PVA/Tris) bionanocomposite films containing graphene oxide (GO) (0.5, 1, 2, and 3 wt%) or graphene (0.5, 1, 2, and 3 wt%) were prepared using a solvent casting method. The scanning electron microscopy results indicated that the dispersion of GO throughout the film matrix was better than that of graphene. The successful formation of new hydrogen bonds between the film matrix and GO was confirmed through the use of Fourier-transform infrared spectroscopy. The tensile strength, elastic modulus, and initial degradation temperature of the films increased, whereas the total soluble mass, water vapor permeability, oxygen permeability, and light transmittance decreased following GO or graphene incorporation. In summary, nanoblending is an effective method to promote the application of FK/PVA/Tris-based blend films in the packaging field.

Poly(phenyl-substituted siloxanes/silsesquioxanes) are obtained by the Piers–Rubinsztajn (PR) reaction of hydrogen-containing siloxanes (HCS) with diphenyldialkoxysilanes such as diphenyldimethoxysilane and diphenyldiethoxysilane catalyzed by tris(pentafluorophenyl)borane. ²⁹Si nuclear magnetic resonance (NMR) spectroscopy, gel permeation chromatography, and refractive index analysis revealed that apart from phenyl substituents and complex structures such as molecular bridges composed of D₂^Ph2[(C₆H₅)₂Si(OSi)₂], structures also existed in these polymers, having high refractive indexes (above 1.50) and high molecular weights (75.60 KDa·mol⁻¹). As revealed by thermogravimetric analysis, these polymers have high thermal stability as well, with temperature at 5% mass loss (T_5%) increasing by 182.5 °C and R_w (residual weight ratio) increasing by 5.17 times from 14.63% to 75.60%, as compared to HCS, exhibiting its potential application as resins for resisting strong heat. Such high-refractive-index and temperature-resistant poly(phenyl-substituted siloxanes/silsesquioxanes) with Si–H and alkoxy functional groups can be used as a good addition-type crosslinking agent with adhesion-promoting properties or a special curing agent that can solidify silicone materials through simultaneous addition and condensation reactions, which has potential application in the light-emitting diode (LED) packaging industry.

The high moisture sensitivity of feather keratin/polyvinyl alcohol/tris(hydroxymethyl)aminomethane (FK/PVA/Tris) blend films hinders their application in the packaging field. Thus, in order to improve the water resistance and mechanical properties of such blend films, we attempted cross-linking the blend film with cross-linking agents such as transglutaminase (TG), CaCl₂, and genipin. Obvious differences in the morphology of the blended films were observed by scanning electron microscopy before and after cross-linking, indicating that cross-linking can inhibit the phase separation of the blend film. Conformational changes in the blend films after cross-linking were detected by Fourier transform infrared spectroscopy. Importantly, from examination of the total soluble mass, contact angle measurements, and water vapor permeability tests, it was apparent that cross-linking greatly improved the water resistance of the blend films, in addition to enhancing the mechanical properties (i.e., tensile strength and elongation at break). However, cross-linking was also found to reduce the oxygen barrier properties of the blend films. Therefore, cross-linking appears to be an effective method for promoting the application of FK/PVA/Tris blend films in the packaging field.

Silicone materials are widely used, from daily life to the military industry. With the advancement of science and technology and the increasing demands of industry, the requirement for high-performance precise structural silicone materials has increased. Therefore, the most important aspect in this field is finding a breakthrough in the synthetic methods. In this review, the latest research developments in controllable morphological structure and composite structure optimized synthesis of silicone materials using the Piers–Rubinsztajn (PR) reaction are summarized. The advantages of the PR reaction compared with traditional synthetic routes to silicone materials are presented. The highly controllable spatial structure of silicone materials and the structural combination of biomass or inorganic materials with silicone materials results in an improvement in performance or function. The morphological control of more complex silicone materials and the synthesis of non-traditional silicone materials with composite structures through the PR reaction will be the main research directions for the development of silicone materials in the future.