Feathers, which contain >90% keratin, are valuable natural protein resources. The aim of this study is to prepare antimicrobial feather keratin (FK)-based nanofibers by incorporating silver nanoparticles (AgNPs). A series of AgNPs-embedded feather keratin/poly(vinyl alcohol)/poly(ethylene oxide) (FK/PVA/PEO) composite nanofibers with varying amounts of AgNPs content were fabricated by electrospinning. Their morphology, crystallinity, thermal stability, tensile property, and antibacterial activity were systematically investigated. The average diameters of composite nanofibers gradually decreased with increases in the amount of AgNPs. The crystallinity, thermal stability, and antibacterial activity of FK/PVA/PEO nanofibers were enhanced by embedding AgNPs. When embedded with 1.2% AgNPs, both the tensile strength and elongation-at-break reached the highest level. This work has the potential to expand the application of FK-based nanofibers in the biomaterial field.

Methoxyl-capped MQ silicone resin (MMQ) was first synthesized by the hydrosilylation of vinyl-containing MQ silicone resin and trimethoxysilane and then used in condensed room-temperature vulcanized (RTV) silicone rubber as a self-reinforced cross-linker. Results show that modified silicone rubber exhibits good light transmission. Compared with unmodified silicone rubber, the hardness, tensile strength and elongation of MMQ at the break are increased by 26.4 A, 2.68 MPa and 65.1%, respectively. In addition, the characteristic temperature of 10% mass loss is delayed from 353.5 °C to 477.1 °C, the temperature at maximum degradation rate is also delayed from 408.9 °C to 528.4 °C and the residual mass left at 800 °C is increased from 1.2% to 27.7%. These improved properties are assigned to the synergistic effect of the rigid structure of MMQ, the formation of a dense cross-linking structure in polymers and the uniform distribution of MMQ cross-linking agent in RTV silicone rubber.

With developments of the electronics industry, more components are being included in electronic devices, which has led to challenges in thermal management. Using reduced graphene oxide embedded with MQ silicone resin (RGO/MQ) nano-aggregates as the composite filler and silicone rubber (SR) as the matrix, a simple approach is designed to prepare RGO/MQ/SR composites. Reduced graphene oxide (RGO) was first used as a substrate for the growth of MQ silicone resin by hybridization, forming sandwich-like micro structured RGO/MQ nano-aggregates successfully. Then, RGO/MQ was integrated into α,ω-dihydroxylpolydimethylsiloxane based on the in situ solvent-free blending method, followed by condensation and vulcanization, fabricating the final RGO/MQ/SR composites. The effective strategy could enhance the adaptability between graphene and silicone matrix under external stimuli at room temperature by embedding nanoscale MQ into the interface of graphene/silicone as the buffer layer. Obvious improvements were found in both thermal conductivity and mechanical properties due to excellent dispersion and interfacial compatibility of RGO/MQ in the host materials. These attractive results suggest that this RGO/MQ/SR composite has potential as a thermal interface material for heat dissipation applications.

Blend films of feather keratin (FK) and synthetic poly(vinyl alcohol) (PVA) that were compatibilized by tris(hydroxymethyl)aminomethane (Tris) were successfully prepared by a solution-casting method. The scanning electron microscopy (SEM) results showed that a phase separation occurred in the FK/PVA/Tris blended system. Analysis by Fourier transform infrared spectroscopy indicated that the main interactions between the three components were hydrogen bonds. In addition, X-ray diffraction analysis showed that the FK/PVA/Tris blend films were partially crystalline. The barrier properties, mechanical properties, and contact angles of the FK/PVA/Tris films were investigated to determine the effects of the PVA and Tris concentrations. More specifically, upon increasing the PVA content, the elongation at break, the hydrophilicity, and the oxygen barrier properties were enhanced. However, at a constant PVA content, an increase in the Tris content caused the oxygen permeability and the contact angle to decrease, while the tensile strength, elongation at break, and oxygen barrier properties were enhanced. These results indicated that the mechanical properties and gas resistance of the FK/PVA/Tris blend films could be successfully improved using the method described herein, confirming that this route provided a convenient and promising means to prepare FK plastics for practical applications.

Microfibril cellulose (MFC), which is detrimental to soil cultivation and environmental protection, is derived from waste pineapple leaves. Hexagonal boron nitride (h-BN) was modified with polydopamine (PDA)—PDA@h-BN named pBN, and then combined with MFC to prepare a novel hybrid powder. The effect of PDA on h-BN and the binding effect between pBN and MFC were characterized by X-ray photoelectron spectroscopy (XPS), Thermogravimetric (TG), scanning electron microscopy (SEM), and Fourier Transform-Infrared (FT-IR). Poly (vinyl alcohol) (PVA) was used as an eco-friendly polymeric matrix to prepare a pBN-MFC-PVA composite film. The mechanical strength, hydrophobicity, and thermal conductivity of the film were studied and the results confirmed that h-BN was chemically modified with PDA and was uniformly distributed along the MFC. The thermal conductivity of the pBN-MFC-PVA composite film increased with the addition of a pBN-MFC novel powder. MFC acted as “guides” to mitigate the h-BN agglomerate. In addition to the possible usage in the pBN-MFC-PVA composite film itself, the pBN-MFC hybrid powder may be a potential filler candidate for manufacturing thermal interface materials and wearable devices or protective materials.

In this study, feather keratin/polyvinyl alcohol/tris(hydroxymethyl)aminomethane (FK/PVA/Tris) bionanocomposite films containing two types of nanoparticles, namely one-dimensional sodium montmorillonite (MMT) clay platelets (0.5, 1, 3, and 5 wt%) and three-dimensional TiO₂ nanospheres (0.5, 1, 3, and 5 wt%), are prepared using solvent casting method. X-ray diffraction studies confirm the completely exfoliated structure of FK/PVA/Tris/MMT nanocomposites. The successful formation of new hydrogen bonds between the hydroxyl groups of the film matrix and the nanofillers is confirmed by Fourier transform infrared spectroscopy. The tensile strength, elongation at break, and initial degradation temperature of the films are enhanced after MMT and TiO₂ incorporation. The water vapor permeability, oxygen permeability, and light transmittance decrease with increase in TiO₂ and MMT contents. In summary, nanoblending is an effective method to promote the application of FK/PVA/Tris blend films in the packaging field.