As a flexible and environmentally friendly technology, bioleaching is widely used to recover base metals from raw materials and industrial waste. This study aimed to test and compare the bioleaching potential of the fungi Aspergillus niger and Penicillium ochrochloron for copper, zinc, and cobalt...

Copper slag, a by-product of copper ore and concentrate smelting, is rich in non-ferrous metals; therefore, it has been considered a valuable raw material in recent years. This study aimed to compare the extraction of zinc, copper, and cobalt from two types of copper slag from a dump located near the village of Eliseyna, Bulgaria, which differ in mineralogical composition and chemical content, using indirect bioleaching with a spent medium of Aspergillus niger and Penicillium ochrochloron. Chemical leaching with sulphuric acid revealed that zinc and cobalt existed mainly as an acidic-soluble phase in both types of copper slag. In contrast, it contained 50–75% of the total copper content. Each fungal species was cultivated for one week, and the biomass and the spent medium were separated a week later. Owing to the production of a higher concentration of citric acid, A. niger facilitated more efficient base metal recovery. However, their effective recovery from the acidic-soluble phase required leaching at a 5% pulp density and supplementing the spent medium with sulphuric acid. The temperature played a secondary role. Conclusions: Non-ferrous metal extraction from copper slag exposed to weathering using a spent medium supplemented with sulphuric acid was achieved under milder leaching conditions and with better selectivity. In contrast, slag unaffected by weathering behaved as a refractory due to the worsened results of base metal extraction under similar experimental conditions.

This study aimed to compare the recovery of non-ferrous metals from a pyrometallurgy copper slag containing 1.93 % Zn, 0.36 % Cu, and 0.09 % Co by spent medium bioleaching of fungi Aspergillus Niger and Penicillium ochrochloron. The fungal species were cultivated for a week; microbial biomass was separated, and the shake-flask technique carried out the leaching. Factors such as temperature, pulp density, the organic acids ratio and the amount of added acidity strongly affected the extraction of the non-ferrous metals from copper slag.

Copper slag, a by-product of copper ore and concentrate smelting, is rich in non-ferrous metals; therefore, it has been considered a valuable raw material in recent years. This study aimed to compare the extraction of zinc, copper, and cobalt from two types of copper slag from a dump located near the village of Eliseyna, Bulgaria, which differ in mineralogical composition and chemical content, using indirect bioleaching with a spent medium of Aspergillus niger and Penicillium ochrochloron. Chemical leaching with sulphuric acid revealed that zinc and cobalt existed mainly as an acidic-soluble phase in both types of copper slag. In contrast, it contained 50-75% of the total copper content. Each fungal species was cultivated for one week, and the biomass and the spent medium were separated a week later. Owing to the production of citric acid at a higher concentration, A. niger facilitated more efficient base metal recovery. However, their effective recovery from the acidic-soluble phase required leaching at a 5% pulp density and supplementing the spent medium with sulphuric acid. The temperature played a secondary role. Conclusions: The non-ferrous metal extraction from copper slag exposed to weathering using a spent medium supplemented with sulphuric acid was achieved under milder leaching conditions and with better selectivity. In contrast, slag unaffected by weathering behaved as a refractory due to the worsened results of base metal extraction under similar experimental conditions.