In this work, an innovative nano-carbon material (N-CM) adsorbent was reported for exploring its adsorption behaviors toward cationic methylene blue (MB) and anionic reactive blue 19 (RB19) pollutants. The proposed N-CM was synthesized by a one-step solvothermal treatment of citric acid and zinc gluconate small precursors. N-CM consists of nanosheets that have an advantageous specific surface area, large sp²/sp³ hybridized domains, and abundant nitrogen/oxygen-containing surface functional groups. The synergistic effects of these features are conducive to the MB and RB19 adsorption. Different from anionic RB19 adsorption (79.54 mg/g) by the cooperative π-π stacking and hydrogen bonding, cationic MB adsorbed onto N-CM mainly by the electrostatic attraction at the natural pH solution (> pH_pzc), with an adsorption capacity up to 118.98 mg/g. Interestingly, both MB and RB19 adsorption conformed to the pseudo-second order kinetic (R² ≥ 0.995) and Langmuir isothermal (R² ≥ 0.990) models, accompanied by similar maximum monolayer adsorption capacities of 120.77 and 116.01 mg/g, respectively. Their adsorption processes exhibited spontaneously endothermic characteristics. Moreover, N-CM showed superior selective capability toward MB in different mixed dye systems, with high removal efficiencies of 73–89%. These results demonstrate that the high-performance carbon adsorbent prepared from small precursors via low-temperature carbonization shows great potentials in wastewater treatment.

Size-controlled azoxystrobin-poly (lactic acid) microspheres (MS) were prepared by an oil/water emulsion solvent evaporation approach. The hydrated mean particle sizes of the MS1, MS2, and MS3 aqueous dispersions were 130.9 nm, 353.4 nm, and 3078.0 nm, respectively. The drug loading and encapsulation efficiency of the azoxystrobin microspheres had a positive relationship with particle size. However, the release rate and percentage of cumulative release were inversely related to particle size. The smaller-sized microspheres had a greater potential to access the target mitochondria. As a result, the more severe oxidative damage of Colletotrichum higginsianum Sacc and higher antagonistic activity were induced by the smaller particle size of azoxystrobin microspheres. The 50% lethal concentrations against Colletotrichum higginsianum Sacc of MS1, MS2, and MS3 were 2.0386 μg/mL, 12.7246 μg/mL, and 21.2905 μg/mL, respectively. These findings reveal that particle size is a critical factor in increasing the bioavailability of insoluble fungicide.

The effective utilization of many conventional pesticide formulations is less than 30%, which can increase the environmental impact of these substances. This degree of waste could be reduced by improving the adhesion of pesticides to foliage. In the present work, a complex comprising tannic acid (TA) and Fe³⁺ ions was used to encapsulate azoxystrobin and avermectin water dispersible granule (WDG) formulations (termed Az-WDG-TA and Av-WDG-TA) to improve adhesion. The treated pesticides exhibited improved photostability as well as sustained continuous release behavior. The retention proportions of the Az-WDG-TA and Av-WDG-TA on cucumber and lettuce foliage were improved by more than 50%. The ability of solutions of these materials to wet foliage was also enhanced after coating, such that the toxicity of Av-WDG-TA to aphids and the antifungal activity of Az-WDG-TA to Fusarium oxysporum were increased by nearly 50%. Given the low cost of TA and Fe³⁺ compounds and the simple synthesis process, this method represents a promising means of producing foliage-adhesive pesticide formulations with increased retention and bioavailability.

Pesticides play key roles in modern agricultural activities. Optimizing pesticide deposition is essential for maximizing utilization efficiency and minimizing unintended environmental impacts. While electrostatic, hydrogen, and covalent interactions have been extensively studied to modulate pesticide adhesion to leaf surfaces, the potential of metal coordination bonding to enhance foliar deposition remains largely unexplored. In our work, abamectin-loaded PLA nanospheres coated in tannic acid (TA) (Abam@PLA) via the metal chelating ability of polyphenols (Abam@PLA-TA) were developed to improve abamectin retention on the surfaces of leaves. The chemical properties and morphological features of Abam@PLA-TA were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FT-IR), and fluorescent imaging. The foliar retention of Abam@PLA-TA demonstrated that the tannic acid coating could significantly improve the adhesion ability and deposition efficiency of pesticides for crop leaves, which was mainly attributed to the hydrogen bonds between the polyphenols of TA and the polar groups of the wax layer. Moreover, Abam@PLA-TA exhibited better photostability capacity compared to the abamectin technical concentrate, which helps to protect light-sensitive pesticides from ultraviolet (UV) decomposition. This strategy opens up a simple but powerful avenue for the design of foliage adhesive systems and a new opportunity for the efficient utilization of pesticides.