Textile-based dye-sensitized solar cells (DSSCs) can be created by building the necessary layers on a textile fabric or around fibers which are afterwards used to prepare a textile layer, typically by weaving. Another approach is using electrospun nanofiber mats as one or more layers. In this work, electrospun polyacrylonitrile (PAN) nanofiber mats coated by a conductive polymer poly(3,4-ethylenedioxythiopene) polystyrene sulfonate (PEDOT:PSS) were used to produce the counter electrodes for half-textile DSSCs. The obtained efficiencies were comparable with the efficiencies of pure glass-based DSSCs and significantly higher than the efficiencies of DSSCs with cotton based counter electrodes. The efficiency could be further increased by increasing the number of PEDOT:PSS layers on the counter electrode. Additionally, the effect of the post treatment of the conductive layers by HCl, acetic acid, or dimethyl sulfoxide (DMSO) on the DSSC efficiencies was investigated. Only the treatment by HCl resulted in a slight improvement of the energy-conversion efficiency.

In recent years the harvesting of renewable energies became of great importance. This led to a rapid development of dye-sensitized solar cells which can be produced from low-purity materials. The best electrical properties are provided by cells prepared using synthetical, ruthenium based dyes. Unfortunately, most of them are toxic and expensive. The anthocyanins extracted for example from hibiscus flowers yield a more cost-effective and eco-friendly alternative to toxic dyes, however, with a loss of solar cell efficiency. In this article the possibility of improvement of the conversion efficiency by modification of the pH value of the dye is investigated. By decrease of the pH value, an increase of efficiency by a factor of two was achieved.

Caffeine is known to influence the absorbance spectrum of anthocyanin dyes. Such dyes are often used as sensitizers in dye-sensitized solar cells (DSSCs). Natural dyes, like anthocyanins, yield only small DSSC efficiencies, but are of high interest since they are usually non-toxic and inexpensive. Here we report on the influence of copigmentation of anthocyanins, taken from commercially available tea, with caffeine. In this way, the efficiencies were increased for measurements with a solar simulator as well as with ambient light. In addition, the well-known pH dependence of the efficiency of DSSCs dyed with anthocyanins was shifted—while a pH value of 1–2 was ideal for pure anthocyanins used as dyes, a higher pH value of 2–3 was sufficient to reach the maximum efficiencies for caffeine-copigmented dyes. This means that instead of reducing the pH value by adding an acid, adding caffeine can also be used to increase the efficiency of DSSCs prepared with anthocyanins. Finally, a comparison of several literature sources dealing with anthocyanin-based DSSCs allows for evaluation of our results with respect to the work of other groups.

Magnetic vortex structures are of high technological relevance due to their possible application in magnetic memory. Moreover, investigating magnetization reversal via vortex formation is an important topic in basic research. Typically, such vortices are only investigated in homogeneous magnetic materials of diverse shapes. Here, we report for the first time on micromagnetic simulation of vortex formation in magnetic bow-tie nanostructures, comprising alternating parts from iron and permalloy, investigated for two different thicknesses and under different angles of the external magnetic field. While no vortex was found in pure permalloy square, nanoparticles of the dimensions investigated in this study and in case of iron only a relatively thick sample allowed for vortex formation, different numbers of vortices and antivortices were found in the bow-tie structures prepared from both materials, depending on the angular field orientation and the sample thickness. By stabilizing more than one vortex in a confined nanostructure, it is possible to store more than one bit of information in it. Our micromagnetic simulations reveal that such bi-material structures are highly relevant not only for basic research, but also for data storage applications.

Dye sensitized solar cells (DSSCs) are silicon free, simply producible solar cells. Longevity, however, is a longstanding problem for DSSCs. Due to liquid electrolytes being commonly used, evaporation of the electrolyte causes a dramatic drop in electric output as cells continue to be used unmaintained. Stopping evaporation has been tried in different ways in the past, albeit with differing degrees of success. In a recent project, a different route was chosen, exploring ways of revitalizing DSSCs after varying periods of usage. For this, we focused on rehydration of the cells using distilled water as well as the electrolyte contained in the cells. The results show a significant influence of these rehydration procedures on the solar cell efficiency. In possible applications of DSSCs in tents etc., morning dew may thus be used for rehydration of solar cells. Refillable DSSCs can also be used in tropical climates or specific types of farms and greenhouses where high humidity serves the purpose of rehydrating DSSCs

Electrospinning can be used to produce nanofiber mats. One of the often used polymers for electrospinning is polyacrylonitrile (PAN), especially for the production of carbon nanofibers, but also for a diverse number of other applications. For some of these applications—e.g., creation of nano-filters—the dimensional stability of the nanofiber mats is crucial. While relaxation processes—especially dry, wet and washing relaxation—are well-known and often investigated for knitted fabrics, the dimensional stability of nanofiber mats has not yet been investigated. Here we report on the wet relaxation of PAN nanofiber mats, which are dependent on spinning and solution parameters such as: voltage, electrode distance, nanofiber mat thickness, and solid content in the solution. Our results show that wet relaxation has a significant effect on the samples, resulting in a dimensional change that has to be taken into account for nanofiber mats in wet applications. While the first and second soaking in pure water resulted in an increase of the nanofiber mat area up to approximately 5%, the dried sample, after the second soaking, conversely showed an area reduced by a maximum of 5%. For soaking in soap water, small areal decreases between approximately 1–4% were measured.