The changes in the cellulose structure of eight Eucalyptus species (E. botryoides, E. globulus, E. grandis, E. maculata, E. propinqua, E. rudis, E. saligna and E. viminalis) in a mild torrefaction (from 160 °C to 230 °C, 3 h) were studied in situ and after cellulose isolation from the wood by solid-state carbon nuclear magnetic resonance (¹³C NMR), wide angle X-ray scattering (WAXS), Fourier transform infrared spectroscopy (FTIR) and by analytic pyrolysis coupled with gas chromatography and mass spectrometry (Py-GC/MS). Changes in molecular weight were assessed by viscosimetry. A small decrease in cellulose crystallinity (ca. 2%–3%) was attributed to its amorphization on crystallite surfaces as a result of acid hydrolysis and free radical reactions resulting in the homolytic splitting of glycosidic bonds. The degree of the cellulose polymerization (DPv) decreased more than twice during the heat treatment of wood. It has been proposed that changes in the supramolecular structure of cellulose and in molecular weight during a heat treatment can be affected by the amount of lignin present in the wood. The limitations of FTIR and Py-GC/MS techniques to distinguish the minor changes in cellulose crystallinity were discussed.

Outdoor wood applications are exposed to several different biotic and abiotic factors, and for that reason, they require protection to increase their service life. Several technologies of wood protection are already commercialized. One of these technologies is thermal modification, which refers to the structural, mechanical, and chemical transformations occurring in the lignocellulosic material when gradually heated up to specific temperature ranges. In the past few years, several researchers have undertaken weathering resistance evaluations on different wood species. Some cases have considered natural exposure in different countries with different climatic conditions, while others focused on artificial exposure under UV and xenon radiation tests. Most works evaluated the weathering effects on the chemical, mechanical and physical, and anatomical shifts compared to the original characteristics of the material. This review has established a considerable lack of studies in the bibliography focusing on abiotic factors, such as the industrial and maritime environment, or even isolated climatic factors such as salt spray (simulating maritime environments) or pollutant gases (simulating industrial environments). This lack of information can be an opportunity for future work. It could help to understand if thermally modified wood is or is not sensitive to pollutant gases or salinity, or to a combination of both. By knowing the degradation mechanisms caused by these factors, it will be possible to study other forms of protection.

Agroforestry industries, such as sugar-alcohol, food, and logging, produce large quantities of waste, used to generate energy from direct burning. The application of other processes, such as torrefaction and briquetting, can increase the profits from the use of agro-industrial waste for energy generation. Briquetting is an alternative for using these wastes, allowing the compaction of the biomass, generating a biofuel with high energy density, and which is more homogeneous and easier to store and transport. The objective of this study was to evaluate the physical and chemical properties of four biomass types (wastes from sawed eucalypt and pine wood, coffee pruning wastes, and sugarcane bagasse) torrefied at 300 °C and compacted (briquetting) at pressures of 6.21, 8.27, and 10.34 MPa. The torrefaction increased the fixed carbon content, ash, and calorific value, and reduced the volatile material content and hygroscopic equilibrium moisture of the biomasses. The volatile material content was lower and the fixed carbon higher in the coffee pruning waste, the ash content higher in the sugarcane bagasse, and the calorific value higher in the pine and eucalypt wood. The briquetting and the torrefaction processes increased the biomass bulk density, and the useful calorific value, respectively, and consequently the energy density of the briquettes produced with torrefied raw material under high pressure. The mechanical properties of the briquettes produced with all materials increased with the compaction pressure. Torrefaction and briquetting increased the energy potential of the biomasses evaluated to produce energy from clean technology.

Wood-based panels made of waste and recycled raw material are lacking of dimensional stability. The aim of this study is to evaluate the potential beneficial effect of heat treatment (HT) on the properties of particleboards produced from waste of Pinus sp. used for packaging. The wood particles were heat treated at 180°C, 200°C and 220°C after grinding, and panels were produced with incorporation of 25%, 50%, 75% and 100% HT particles. The materials served as reference were particles without HT. Mass loss at 180°C and 200°C was small but increased significantly to 10.6% at 220°C. The HT caused a partial degradation of hemicelluloses, thereby the relative lignin content increased from 29.7% to 37.8% for the HT₂₂₀°_C samples. Thermogravimetry revealed higher thermal stability of the HT particles. The equilibrium moisture content decreased with HT, e.g. panels with HT_220°C showed 30% lower compared to the reference. Swelling of the panels was lowered by 30% (panel with 75% HT material) compared to the reference. The results with HT pine were successful in terms of dimensional stability and lower hygroscopicity; however, the panels lost some strength properties.

Heat treatment improves some wood properties namely: equilibrium moisture, dimensional stability and durability and mechanical properties. In this study, the heat treatment was applied to woods of three natural species from Brazil: Aspidosperma populifolium (peroba mica), Dipteryx odorata (cumaru) and Mimosa scabrella (bracatinga). The woods were heated in an oven under vacuum and under nitrogen, at 180, 200, and 220°C for one hour. The untreated and heat-treated woods were characterized in relation to equilibrium moisture content, basic density, shrinkage, Janka hardness, and bending MOR and MOE according to NBR 7190 standards. All the thermal rectified woods showed a reduction in the hygroscopic equilibrium content, especially when the heating was under vacuum from 13-15% in the untreated woods to 1-3% for vacuum treatment at 220 °C. The dimensional stability was improved to only a small extent e.g. volumetric shrinkage tended to decrease with increasing temperature. The mechanical properties were affected differently for the three wood species. Heat-treated cumarushowed increased Janka hardness, MOR and MOE; and peroba mica increased MOR and MOE but not Janka hardness; while bracatinga was less influenced by the heat treatmentinfo:eu-repo/semantics/publishedVersio