Chloride ingress can lead to serious degradation of various materials and structures. Continuous measurements of local chloride concentrations is thus of uttermost importance for laboratory research, monitoring of structures, and predictions of the residual life span for the most common building materials. This work investigates the applicability of Ag/AgCl ion-selective electrodes for the non-destructive continuous measurement of local chloride concentrations in concrete and stone when exposed to chloride-bearing environments such as seawater. The work studies the stability of Ag/AgCl ion-selective electrodes in neutral and alkaline solutions and the sensitivity to the main interfering ions coming from the environment and from the material itself. The results indicate negligible interference from fluoride, sulfate, and hydroxyl but considerable from bromide and sulfide. In chloride-free alkaline solutions, Ag/AgCl ion-selective electrodes are not stable over time, but—upon chloride arrival—they permit again reliable measurements of the chloride concentration. The results concerning interference are discussed by taking into account typical exposure environments and it is concluded that the ion-selective electrodes can satisfactorily be used to monitor chloride concentrations in built structures made out of concrete or stone.

Both the free chloride concentration and the pH of the concrete pore solution are highly relevant parameters that control corrosion of the reinforcing steel. In this paper, we present a method to continuously monitor these two parameters in-situ. The approach is based on a recently developed electrode system that consists of several different potentiometric sensors as well as a data interpretation procedure. Instrumented mortar specimens containing different amounts of admixed chlorides were exposed to accelerated carbonation, and changes in free chloride concentration and pH were monitored simultaneously over time. The results revealed the stepwise decrease in pH as well as corresponding increases in free chlorides, resulting from the release of bound chlorides. For a pH drop of about 1 unit (from pH 13.5 down to pH 12.5), the free chloride concentration increased up to 1.5-fold. We continuously quantified the ratio Cl⁻/OH⁻ that increased steeply with time, and was found to exceed a critical corrosion threshold long before carbonation can be detected with traditional indicator spray testing, even at admixed chloride contents in the order of allowable limits. These results can strongly influence the decision-making in engineering practice and it is expected to significantly improve condition assessments of reinforced concrete structures.