The electrical and electromechanical responses of ~200 µm thick extruded nanocomposite films comprising of 4 wt.% and 5 wt.% multiwall carbon nanotubes mixed with polypropylene are investigated under an alternating current (AC) and compared to their direct current (DC) response. The AC electrical response to frequency (f) and strain (piezoimpedance) is characterized using two configurations, namely one that promotes resistive dominance (resistive configuration) and the other that promotes the permittivity/capacitive contribution (dielectric configuration). For the resistive configuration, the frequency response indicated a resistive–capacitive (RC) behavior (negative phase angle, θ), with a significant contribution of capacitance for frequencies of 10⁴ Hz and above, depending on the nanotube content. The piezoimpedance characterization in the resistive configuration yielded an increasing impedance modulus (|Z|) and an increasing (negative) value of θ as the strain increased. The piezoimpedance sensitivity at f = 10 kHz was ~30% higher than the corresponding DC piezoresistive sensitivity, yielding a sensitivity factor of 9.9 for |Z| and a higher sensitivity factor (~12.7) for θ. The dielectric configuration enhanced the permittivity contribution to impedance, but it was the least sensitive to strain.

The design and analysis of a device to measure the burst strength (strength under a state of pure radial internal pressure) and compliance of vascular grafts and flexible pressurized tubes is presented. The device comprises three main sections, viz., a clean air-dry pressure controller, a test specimen holder, and automated software for control and data collection. Air pressure is controlled by means of a valve and a dedicated mechanism allowing reaching up to 120 psi in increments of 1 psi, and recording pressure changes with 0.04 psi resolution. The circumferential strain is determined by measuring the radial displacement of the vascular graft using an optical arrangement capable of determining a maximum radial displacement of 10 mm with 0.02 mm resolution. The instrument provides a low uncertainty in compliance (±0.32%/100 mm Hg⁻¹) and burst strength measurements. Due to its simplicity, the device can easily be reproduced in other laboratories contributing to a dedicated instrument with high resolution at low cost. The reliability of the apparatus is further confirmed by conducting finite element analysis, elasticity solutions for pressurized cylinders, and testing of small diameter vascular grafts made of a commercial aliphatic polyurethane tested under radial internal pressure.