The purpose of this work was to deposit Zn-containing films on Si substrates using the commercial atmospheric pressure plasma jet “kINPen’09.” In preliminary experiments Zn-containing films were deposited on the silicon substrates immersed in water solutions of Zn(NO₃)₂•6H₂O salt. The surface composition of deposited films was analyzed by the XPS (X-ray photoelectron spectroscopy) technique while the bulk composition was studied by means of XRD (X-ray diffraction) mesurements. The film thickness was measured by a profilometer. We have determined that the concentration of the zinc nitrate solution as well as changes in the deposition time resulted in a large fluctuation of the deposited film thickness. However, the successful deposition of the Zn-containing films on the Si substrate was definitely confirmed.

Stable antimicrobial nisin layers were prepared on the carrying medium-polyvinyl alcohol (PVA) films, crosslinked by glutaric acid. Surface plasma dielectric coplanar surface barrier discharge (DCSBD) modification of polyvinyl alcohol was used to improve the hydrophilic properties and to provide better adhesion of biologically active peptide-nisin to the polymer. The surface modification of films was studied in correlation to their cross-linking degree. Nisin was attached directly from the salt solution of the commercial product. In order to achieve a stable layer, the initial nisin concentration and the following release were investigated using chromatographic methods. The uniformity and stability of the layers was evaluated by means of zeta potential measurements, and for the surface changes of hydrophilic character, the water contact angle measurements were provided. The nisin long-term stability on the PVA films was confirmed by tricine polyacrylamide gel electrophoresis (SDS-PAGE) and by antimicrobial assay. It was found that PVA can serve as a suitable carrying medium for nisin with tunable properties by plasma treatment and crosslinking degree.