Segregation defects greatly affect the service performance and working life of castings during the vacuum arc remelting (VAR) process. However, the corresponding research on the prediction of segregation defects is still not comprehensive. Through considering the influence of water-cooled crucible on the electromagnetic field inside an ingot, a full-scale model for the comprehensive prediction of freckles and macrosegregation defects during the VAR process is developed in this paper. The macroscopic solute transport phenomenon and the segregation behavior of Ni-5.8 wt% Al-15.2 wt% Ta alloy are predicted. The results indicate that the freckles are mainly concentrated in the lower region of the ingot. With the growth of the ingot, the solute enrichment channels gradually develop into solute enrichment regions, and the channel segregation evolves into macrosegregation. The Lorentz force mainly affects the flow pattern at the top of the molten pool, while the complex flow of multiple vortices is dominated by thermosolutal buoyancy. The maximum and minimum relative segregation ratio inside the ingot can reach 290% and −90%, respectively, and the positive segregation region accounts for about 79% of the total volume. This paper provides a new perspective for understanding the segregation behavior inside the ingot by studying the segregation evolution during the VAR process.

Heat treatments, including solution treatment and isothermal heat treatment, were conducted to investigate the grain boundary serration of GH4975 superalloy. The two different heat treatment processes could both promote the formation of serrated grain boundaries within the present temperature and soaking time ranges, provided that the cooling rates were controlled to be quite slow. The samples subjected to furnace cooling exhibited a more obvious serrated grain boundary morphology by comparison with those subjected to air cooling. The interaction between precipitated phases and grain boundaries was focused to explore the formation mechanisms of serrated grain boundaries within GH4975 superalloy. Heat treatment temperature and soaking time strongly affected the morphology and size of precipitated phases, and consequently influenced the formation of serrated grain boundaries. The directional growth of grain boundary precipitates and its pinning effects on the migration of grain boundaries also affected the grain boundary morphology.

In order to meet the requirement of high-quality ingots, the vibrating electrode technique in the electroslag remelting (ESR) process has been proposed. Non-metallic inclusions in ingots may cause serious defects and deteriorate mechanical properties of final products. Moreover, the dimension, number and distribution of non-metallic inclusions should be strictly controlled during the ESR process in order to produce high-quality ingots. A transient 2-D coupled model is established to analyze the motion behavior of inclusions in the lab-scale ESR process with a vibrating electrode, especially under the influence of the vibration frequency, current, slag layer thickness, and filling ratio, as well as type and diameter of inclusions. Simulation model of inclusions motion behavior is established based on the Euler-Lagrange approach. The continuous phase including metal and slag, is calculated based on the volume of fluid (VOF) method, and the trajectory of inclusions is tracked with the discrete phase model (DPM). The vibrating electrode is simulated by the user-defined function and dynamic mesh. The results show that when the electrode vibration frequency is 0.25 Hz or 1 Hz, the inclusions will gather on one side of the slag layer. When it increases from 0.25 Hz to 1 Hz, the removal ratio of 10 μm and 50 μm inclusions increases by 5% and 4.1%, respectively. When the current increases from 1200 A to 1800 A, the flow following property of inclusions in the slag layer becomes worse. The removal ratio of inclusions reaches the maximum value of 92% with the current of 1500 A. The thickness of slag layer mainly affects the position of inclusions entering the liquid-metal pool. As the slag layer thickens, the inclusions removal ratio increases gradually from 82.73% to 85.91%. As the filling ratio increases, the flow following property of inclusions in the slag layer is enhanced. The removal ratio of 10 μm inclusions increases from 94.82% to 97%. However, for inclusions with a diameter of 50 μm, the maximum removal ratio is 96.04% with a filling ratio of 0.46. The distribution of 50 μm inclusions is significantly different, while the distribution of 10 μm inclusions is almost similar. Because of the influence of a vibrating electrode, 10 μm ${\mathrm{Al}}_2{\mathrm{O}}_3$ and $\mathrm{MnO}$ have a similar removal ratios of 81.33% and 82.81%, respectively.

Structural characteristics and design requirements for the integration of the integral rotor and disc shaft of the engine, the welding quality, and mechanical properties of superalloy weldments have received more and more attention in recent years. Inertia friction welding (IFW) was carried out with the typical fiber structure of the solid solution GH4065A alloy as the research object, the microstructure evolution rules of the plastic deformation zone (PDMZ), the thermally affected zone (TMAZ), and the welding zone (WZ) were studied, and the formation mechanism of metallurgical joints was explored. The size difference of the γ′ phase at the grain boundary and in the fiber structure was revealed. The reason is that the γ′ phase located at the grain boundary has lower diffusion activation energy and higher diffusion rate. The microhardness and tensile properties of the IFW joints were explored, the study found that the microhardness of the TAMZ is the highest, followed by the PDMZ and the WZ. The tensile test results show that with the increase in temperature, the fracture position shifts from the BM to the WZ, the microstructure at the fracture changed significantly, and the yield strength decreased from 1372 to 1085 MPa.