There is far less study of the refining effect of super gravity fields on solidification structures of metals than of the effects of electrical currents, magnetic and ultrasonic fields. Moreover, the refining mechanisms of super gravity are far from clear. This study applied a super gravity field to Al-Cu alloys to investigate its effect on refining their structures and the mechanism of interaction. The experimental results showed that the solidification structure of Al-Cu alloys can be greatly refined by a super gravity field. The major refining effect was mainly achieved when super gravity was applied at the initial solidification stage; only slight refinement could be obtained towards the end of solidification. No refinement was obtained by the super gravity treatment on pure liquid or solid stages. The effectiveness of super gravity results from its promoting the multiplication of crystal nuclei, which we call “Heavy Crystal Rain”, thereby greatly strengthening the migration of crystal nuclei within the alloy. Increasing the solute Cu content can increase nucleation density and restrict the growth of crystals, which further increases the refining effect of super gravity. Within this paper, we also discuss the motile behavior of crystals in a field of super gravity.

This article reviews the research and development focus of metallic glasses in the field of biomedical applications. Metallic glasses exhibit a short-range ordered and long-range disordered glassy structure at the microscopic level, devoid of structural defects such as dislocations and grain boundaries. Therefore, they possess advantages such as high strength, toughness, and corrosion resistance, combining characteristics of both metals and glasses. This novel alloy system has found applications in the field of biomedical materials due to its excellent comprehensive performance. This review discusses the applications of Ti-based bulk metallic glasses in load-bearing implants such as bone plates and screws for long-term implantation. On the other hand, Mg-based metallic glasses, owing to their degradability, are primarily used in degradable bone nails, plates, and vascular stents. However, metallic glasses as biomaterials still face certain challenges. The Young’s modulus value of Ti-based metallic glasses is higher than that of human bones, leading to stress-shielding effects. Meanwhile, Mg-based metallic glasses degrade too quickly, resulting in the premature loss of mechanical properties and the formation of numerous bubbles, which hinder tissue healing. To address these issues, we propose the following development directions: (1) Introducing porous structures into titanium-based metallic glasses is an important research direction for reducing Young’s modulus; (2) To enhance the bioactivity of implant material surfaces, the surface modification of titanium-based metallic glasses is essential. (3) Developing antibacterial coatings and incorporating antibacterial metal elements into the alloys is essential to maintain the long-term effective antibacterial properties of metallic biomaterials. (4) Corrosion resistance must be further improved through the preparation of composite materials, while ensuring biocompatibility and safety, to achieve controllable degradation rates and degradation modes.

Amounts of rare earth oxides were transferred into mold fluxes for the continuous casting of rare earth alloyed heavy railway steels. B₂O₃ was added to improve the viscosity properties and the crystallization behavior of this traditional mold flux. Thus, in this paper, effects of B₂O₃ on viscosity, structure, and crystallization of CeO₂-bearing mold fluxes for casting rare earth alloyed heavy railway steels were investigated by rotating cylinder method, Raman spectroscopy, and magic angle spinning nuclear magnetic resonance (MAS NMR). Experimental results revealed that with the addition of B₂O₃, viscosity values of mold fluxes at some certain temperatures decreased significantly. By analyzing the structure of glassy mold fluxes, it can be observed that B₂O₃ behaved as a network-forming oxide within the studied system. However, the introduction of the weak bond energy of B–O and the transition from four-fold coordination boron to three-fold coordination boron with loose structural units mainly reduced the viscosity. Moreover, results of X-ray diffraction (XRD) and differential scanning calorimetry (DSC) confirmed that B₂O₃ decreased the crystallization of the crystal phase Na₄Ca₄(Si₆O₁₈) and the solidus temperature of mold fluxes. Thus, these results obtained can provide guidelines for designing new mold fluxes for casting rare earth alloyed steels.

Atomic oxygen in the low Earth orbit (LEO) environment is highly oxidizing. Due to the high flight speed of spacecraft, the relative kinetic energy of high-flux atomic oxygen bombarding the spacecraft surface can reach up to about 5 eV. Therefore, atomic oxygen is one of the most dangerous space environment factors in LEO, which seriously affects the safe operation and service life of spacecraft in orbit. In order to meet the requirements for the high reliability and long lifetime of spacecraft, effective protection measures must be taken on their sensitive surfaces. Siloxane is a coating with an organic–inorganic hybrid structure. Compared with SiO₂ and other inorganic atomic oxygen protective coatings, it has better flexibility and is better at anti-atomic oxygen performance. In this paper, the plasma polymerization deposition technique was used to prepare large-area siloxane coatings on different substrates with different thicknesses for improving atomic oxygen resistance by optimizing the process parameters. The thickness of the coating was measured by different methods, and the results showed that the thickness distribution was consistent. By observing the surface morphology of the coating, it was uniform and compact without obvious defects, so the uniformity of large-area coating was also ideal. The adhesion and heat/humidity resistance of siloxane coatings were examined by pull-off testing and damp-heat testing, respectively. The results showed that the siloxane coatings with a thickness of about 400 nm exhibited better physical properties. At the same time, the ground simulation testing of atomic oxygen confirmed that siloxane coatings with a thickness of 418 nm presented the best performance of atomic oxygen resistance. The atomic oxygen erosion yield of siloxane coatings with a thickness of 418 nm was as low as 5.39 × 10⁻²⁷ cm³/atoms, which was three orders of magnitude lower than that of the uncoated Kapton substrate and presented a good anti-atomic oxygen performance. Meanwhile, it has also successfully passed the damp-heat test. The coating thickness is only several hundred nanometers and does not increase the weight of the spacecraft, which makes it a relatively ideal LEO atomic oxygen protection material. Furthermore, a possible mechanism was proposed to explicate the physicochemical process of atomic oxygen attacking the coating materials.

The CaO-Al₂O₃-based mold fluxes are proposed for the Ce-bearing heavy rail steel continuous casting because of the low reactivity. Effects of CeO₂ on the melting temperature, the viscous property, and the crystallization behavior of the CaO-Al₂O₃-Li₂O-B₂O₃ mold fluxes were studied using hemisphere melting point method, rotating cylinder method, and X-ray diffraction (XRD) in the present work. The microstructure of the mold fluxes was analyzed by Fourier-transform infrared spectroscopy (FTIR). The results revealed that the addition of CeO₂ would increase the melting temperature, but decrease the viscosity at each temperature due to its influence on increasing the depolymerization of the mold fluxes at high temperature. The precipitation of CaO was restrained and CaCeAlO₄ generated with increasing CeO₂ content since the crystal phases were affected by the microstructure of the melts. The change of the crystalline phases in mold fluxes influences the break temperature and the viscosity of the mold fluxes below the break temperature. These results obtained can provide guidelines for designing new mold fluxes for casting rare earth alloy heavy rail steels.